|Número de publicación||US6777089 B1|
|Tipo de publicación||Concesión|
|Número de solicitud||US 09/926,366|
|Número de PCT||PCT/EP2000/003221|
|Fecha de publicación||17 Ago 2004|
|Fecha de presentación||11 Abr 2000|
|Fecha de prioridad||21 Abr 1999|
|También publicado como||DE19917965A1, DE50007387D1, EP1171298A1, EP1171298B1, EP1171298B2, US7241494, US7479322, US20040224162, US20070184294, US20070284775, WO2000063015A1|
|Número de publicación||09926366, 926366, PCT/2000/3221, PCT/EP/0/003221, PCT/EP/0/03221, PCT/EP/2000/003221, PCT/EP/2000/03221, PCT/EP0/003221, PCT/EP0/03221, PCT/EP0003221, PCT/EP003221, PCT/EP2000/003221, PCT/EP2000/03221, PCT/EP2000003221, PCT/EP200003221, US 6777089 B1, US 6777089B1, US-B1-6777089, US6777089 B1, US6777089B1|
|Inventores||Rainer Königer, Erich Beck, Achim Grefenstein, Reinhold Schwalm, Margit Veeh, Claudia Vogel, Walter Aichholzer, Thomas Gruber, Karl Holdik|
|Cesionario original||Basf Aktiengesellschaft, Daimlerchrysler Ag|
|Exportar cita||BiBTeX, EndNote, RefMan|
|Citas de patentes (16), Citada por (32), Clasificaciones (63), Eventos legales (4)|
|Enlaces externos: USPTO, Cesión de USPTO, Espacenet|
The invention relates to a radiation-curable composite layered sheet or film comprising at least one substrate layer and one outer layer, said outer layer being composed of a radiation-curable composition having a glass transition temperature of more than 40° C.
The specification further relates to a process for producing the radiation-curable composite layered sheet or film and to a process for producing moldings coated with said sheet or film.
DE-A-196 28 966 and DE-A-196 54 918 disclose dry-paint films where the paint has a glass transition temperature of less than 40° C. Curing requires two steps: a partial cure before the film is adhesively bonded to substrates, and the final cure thereafter.
EP-A-361 351 likewise discloses a dry-paint film. Here, the film is radiation-cured before being applied to the substrate moldings.
DE-A-196 51 350 (O.Z. 47587) describes composite layered sheets and films which consist of thermoplastic materials and do not have a radiation-curable coating.
A disadvantage of the radiation-curable dry-paint films known to date is that two or more steps are frequently required to effect the radiation cure, as described in DE-A-196 28 966. Where the film is fully radiation-cured prior to the coating operation, it often becomes brittle and difficult to deform, which is deleterious to its further processing.
With existing radiation-curable films, the coated moldings often lack sufficient scratch resistance and sufficient elasticity when worked on mechanically. It is an object of the present invention to provide radiation-curable composite layered sheets or films which are easy to process and which lend themselves to the coating of moldings by extremely simple techniques. The coated moldings are to have good mechanical properties, effective resistance to external influences, such as a good weathering stability, for example, and in particular are to be mechanically stable—having, for example, good scratch resistance and high elasticity.
We have found that this object is achieved by the radiation-curable composite layered sheet or film defined at the outset and referred to for short as film hereinafter. We have also found processes for coating moldings with the film, and the coated moldings.
The film must include a substrate layer and an outer layer which is applied to the substrate layer directly or, where there are further interlayers, indirectly.
The outer layer is radiation-curable. Accordingly, the outer layer composition used is radiation-curable and comprises groups curable by a free-radical or ionic mechanism (curable groups for short). Preference is given to free-radically curable groups.
The radiation-curable composition is preferably transparent. After curing has been accomplished, as well, the outer layer is preferably transparent: that is, it is a clearcoat layer.
A key constituent of the radiation-curable compositions is the binder, which by filming forms the outer layer.
The radiation-curable composition preferably comprises a binder selected from
i) polymers containing ethylenically unsaturated groups
ii) mixtures of i) with ethylenically unsaturated compounds of low molecular mass
iii) mixtures of saturated thermoplastic polymers with ethylenically unsaturated compounds.
Examples of suitable polymers include those of ethylenically unsaturated compounds, but also polyesters, polyethers, polycarbonates, polyepoxides or polyurethanes.
They suitably include unsaturated polyester resins, which consist essentially of polyols, especially diols, and polycarboxylic acid, especially dicarboxylic acid, where one of the esterification components contains a copolymerizable, ethylenically unsaturated group. Examples of the components in question include maleic acid, fumaric acid, and maleic anhydride.
Preference is given to polymers of ethylenically unsaturated compounds, such as are obtained in particular by means of free-radical addition polymerization.
The free-radical addition polymers include, in particular, polymers composed of more than 40% by weight, with particular preference more than 60% by weight, of acrylic monomers, particularly C1-C8, preferably C1-C4, alkyl (meth)acrylates. By way of ethylenically unsaturated groups, the polymers include in particular (meth)acrylic groups. These groups may be attached to the polymer by, for example, reacting (meth)acrylic acid with epoxide groups in the polymer (e.g., by using glycidyl (meth)acrylate as a comonomer).
Preference is likewise given to polyurethanes. Their unsaturated groups are again preferably (meth)acrylic groups, attached to the polyurethane by reacting hydroxyalkyl (meth)acrylates with isocyanate groups, for example.
The polymers i) per se can be processed as thermoplastics.
The unsaturated polymers i) may also be used in mixtures with ethylenically unsaturated compounds of low molecular mass.
Low molecular mass compounds in this context are compounds having a number average molecular weight of less than 2000 g/mol (as determined by gel permeation chromatography using a polystyrene standard).
Suitable examples include free-radically polymerizable compounds containing only one ethylenically unsaturated, copolymerizable group.
By way of example, mention may be made of C1-C20 alkyl (meth)acrylates, vinylaromatics having up to 20 carbon atoms, vinyl esters of carboxylic acids containing up to 20 carbon atoms, ethylenically unsaturated nitriles, vinyl ethers of alcohols containing from 1 to 10 carbon atoms, and aliphatic hydrocarbons having from 2 to 20, preferably from 2 to 8, carbon atoms and 1 or 2 double bonds.
Preferred alkyl (meth)acrylates are those with a C1-C10 alkyl radical, such as methyl methacrylate, methyl acrylate, n-butyl acrylate, ethyl acrylate and 2-ethylhexyl acrylate.
Also suitable, in particular, are mixtures of the alkyl (meth)acrylates.
Examples of vinyl esters of carboxylic acids having from 1 to 20 carbon atoms are vinyl laurate, vinyl stearate, vinyl propionate, and vinyl acetate.
Examples of suitable vinylaromatic compounds are vinyltoluene, α-butylstyrene, 4-n-butylstyrene, 4-n-decylstyrene, and preferably styrene.
Examples of nitrites are acrylonitrile and methacrylonitrile.
Examples of suitable vinyl ethers are vinyl methyl ether, vinyl isobutyl ether, vinyl hexyl ether, and vinyl octyl ether.
As nonaromatic hydrocarbons having from 2 to 20, preferably from 2 to 8, carbon atoms and one or two olefinic double bonds, mention may be made of butadiene, isoprene, and also ethylene, propylene, and isobutylene.
Compounds contemplated include preferably free-radically polymerizable compounds containing two or more ethylenically unsaturated groups.
The compounds in question are particularly (meth)acrylate compounds, with preference being given in each case to the acrylate compounds: i.e., the derivatives of acrylic acid.
Preferred (meth)acrylate compounds contain from 2 to 20, more preferably from 2 to 10, and with very particular preference from 2 to 6, copolymerizable, ethylenically unsaturated double bonds.
As (meth)acrylate compounds mention may be made of (meth)acrylates and in particular acrylates of polyfunctional alcohols, especially those which contain no functional groups other than the hydroxyl groups or, if having further functional groups, contain only ether groups. Examples of such alcohols include difunctional alcohols, such as ethylene glycol and propylene glycol, and their higher condensation analogs, such as diethylene glycol, triethylene glycol, dipropylene glycol, tripropylene glycol, etc., butanediol, pentanediol, hexanediol, neopentyl glycol, alkoxylated phenolic compounds, such as ethoxylated and/or propoxylated bisphenols, cyclohexanedimethanol, alcohols with a functionality of three or more, such as glycerol, trimethylolpropane, butanetriol, trimethylolethane, pentaerythritol, dimethylolpropane, dipentaerythritol, sorbitol, mannitol, and the corresponding alkoxylated alcohols, especially ethoxylated and propoxylated alcohols.
The alkoxylation products are obtainable conventionally by reacting the above alcohols with alkylene oxides, especially ethylene oxide or propylene oxide. With preference the degree of alkoxylation per hydroxyl group is from 0 to 10, i.e., 1 mol of hydroxyl group may be alkoxylated preferably with up to 10 mol of alkylene oxides.
(Meth)acrylate compounds further include polyester (meth)acrylates, which are the (meth)acrylic esters of polyesterols.
Examples of suitable polyesterols are those such as may be prepared by esterifying polycarboxylic acids, preferably dicarboxylic acids, with polyols, preferably diols. The starting materials for such hydroxyl-containing polyesters are known to the skilled worker. As dicarboxylic acids preferential use may be made of succinic acid, glutaric acid, adipic acid, sebacic acid, o-phthalic acid, their isomers and hydrogenation products, and also esterifiable derivatives, such as anhydrides or dialkyl esters of said acids. Suitable polyols include the abovementioned alcohols, preferably ethylene glycol, 1,2- and 1,3-propylene glycol, 1,4-butanediol, 1,6-hexanediol, neopentyl glycol, and cyclqhexanedimethanol, and also polyglycols of the ethylene glycol and propylene glycol types.
Polyester (meth)acrylates may be prepared in a plurality of stages or else in a single stage, as described, for example, in EP 279 303, from acrylic acid, polycarboxylic acid, and polyol.
Examples of suitable saturated thermoplastic polymers include polymethyl methacrylate, polystyrene, high-impact polymethyl methacrylate, high-impact polystyrene, polycarbonate and polyurethanes.
Radiation-curability is ensured by adding an ethylenically unsaturated, radiation-curable compound. This may be one of the compounds listed under i) and/or ii).
A key feature of the binder i) to iii) is that its glass transition temperature (Tg) is more than 40° C., preferably more than 50° C., and with particular preference more than 60° C. In general, the Tg will not exceed a level of 130° C. (The figures relate to the binder before radiation curing.)
The glass transition temperature, Tg, of the binder may be determined by the DSC (differential scanning calorimetry) method in accordance with ASTM 3418/82.
The amount of the curable groups, i.e., the ethylenically unsaturated groups, is preferably from 0.001 to 0.2 mol, with particular preference from 0.005 to 0.15 mol, with very particular preference from 0.01 to 0.1 mol, per 100 g of binder (solids; that is, without water or other solvents).
The binder preferably has a viscosity of from 0.02 to 100 Pas at 140° C. (as determined in a rotational viscometer).
The radiation-curable compositions may include further constituents. Particular mention may be made of photoinitiators, leveling agents, and stabilizers. For outdoor use, i.e., for coatings directly exposed to daylight, the compositions will particularly include UV absorbers and free-radical scavengers.
UV absorbers convert UV radiation into heat energy. Known UV absorbers include hydroxybenzophenones, benzotriazoles, cinnamic esters, and oxalanilides.
Free-radical scavengers bind free-radical intermediates that are formed. Major free-radical scavengers include sterically hindered amines, known as HALS (hindered amine light stabilizers).
For outdoor applications, the overall UV absorber and free-radical scavenger content is preferably from 0.1 to 5 parts by weight, with particular preference from 0.5 to 4 parts by weight, based on 100 parts by weight of the radiation-curable compounds.
Moreover, besides radiation-curable compounds, the radiation-curable composition may further include compounds which contribute to curing by other chemical reactions. Suitable examples include polyisocyanates, which crosslink with hydroxyl or amino groups.
The radiation-curable composition may be in water-free and solvent-free form, or in the form of a solution or dispersion.
Preference is given to water- and solvent-free radiation-curable compositions, or aqueous solutions or aqueous dispersions.
Particular preference is given to water- and solvent-free radiation-curable compositions.
The radiation-curable composition is thermoplastically deformable and in particular may be extruded.
The above radiation-curable compositions form the outer layer. The layer thickness (after drying and curing) is preferably from 10 to 100 μm.
The substrate layer serves as a support and is intended to ensure that the composite as a whole remains permanently tough.
The substrate layer consists preferably of a thermoplastic polymer, particularly polymethyl methacrylates, polybutyl methacrylates, polyurethanes, polyethylene terephthalates, polybutylene terephthalates, polyvinylidene fluorides, polyvinyl chlorides, polyesters, polyolefins, polyamides, polycarbonates (PC), acrylonitrile-butadiene-styrene (ABS) polymers, acrylic-styrene-acrylonitrile (ASA) copolymers, acrylonitrile-ethylene-propylene-diene-styrene copolymers (A-EPDM), polyether imides, polyether ketones, polyphenylene sulfides, polyphenylene ethers or mixtures thereof.
Preference is given to ASA, especially in accordance with DE 19 651 350, and to the ASA/PC blend. Preference is likewise given to polymethyl methacrylate (PMMA) or impact-modified PMMA.
The layer thickness is preferably from 50 μm up to 5 mm. Particular preference, especially when the substrate layer is injection-backmolded, is given to thicknesses of from 100 to 1000 μm, in particular from 100 to 500 μm.
The polymer of the substrate layer may comprise additives, especially fillers or fibers. The substrate layer may also be colored, in which case it may also act as a coloring layer.
The film may include further layers in addition to the outer layer and the substrate layer.
Suitable examples include coloring interlayers or further layers of thermoplastic material (thermoplastic interlayers), which strengthen the film or serve as release layers.
Thermoplastic interlayers may be made of the polymers listed above under Substrate layer.
Particular preference is given to polymethyl methacrylate (PMMA), preferably impact-modified PMMA. Mention may also be made of polyurethane. Coloring layers may likewise consist of said polymers. They include dyes or pigments which are distributed in the polymer layer.
One preferred film has, for example, the following layer structure, the alphabetical sequence corresponding to the spatial disposition:
A) outer layer
B) thermoplastic interlayer (optional)
C) coloring interlayer (optional)
D) substrate layer
E) adhesive layer (optional)
On the reverse side (reverse for short) of the substrate layer (i.e., the side facing the article to be coated) there may have been applied an adhesive layer, where the film is to be bonded adhesively to the substrate.
Applied to the transparent outer layer there may be a protective layer, e.g., a removable film, which prevents unintended curing. Its thickness may amount, for example, to from 50 to 100 μm. The protective layer may be composed, for example, of polyethylene or polyterephthalate. The protective layer may be removed prior to irradiation.
Alternatively, irradiation may take place through the protective layer; for this, the protective layer must be transparent in the irradiation wavelength range.
The overall thickness of the film is preferably from 50 to 1000 μm.
The production of a composite from the layers B) to D) may take place, for example, by coextrusion of all or some of the layers.
For coextrusion, the individual components are fluidified in extruders and, using special means, are contacted with one another in such a way as to give the films having the layer sequence described above. For example, the components may be coextruded through a slot die. This process is elucidated in EP-A2-0 225 500. As a supplement to the processes described herein, it is also possible to use the process known as adapter coextrusion.
The composite may be produced by conventional processes, for example, by coextrusion, as described above, or by lamination of the layers, in a heatable nip, for example. In this way it is possible first of all the produce a composite of the layers except for the outer layer, and then to apply the outer layer by conventional techniques.
The radiation-curable composition may be applied to the substrate layer or the composite in a simple way, by casting, rolling, knife coating, spraying, etc., for example, and dried where appropriate.
Preference is given to extruding the radiation-curable composition, i.e., the outer layer. Where appropriate, the radiation-curable composition may also be coextruded with one or more further layers.
In the case of extrusion (including coextrusion) of the radiation-curable compositions, the preparation of the radiation-curable composition by mixing of its constituents, and the preparation of the outer layer, may take place in one operation.
To this end, thermoplastic constituents, e.g., unsaturated polymers i) or saturated polymers iii) (see above), may first of all be melted in the extruder. The requisite melting temperature depends on the polymer in question. After the melting operation, preferably, the further constituents may be metered in, especially radiation-curable compounds ii) of low molecular mass (see above). The compounds act as plasticizers, thereby reducing the temperature at which the composition is in melt form. The temperature on addition of the radiation-curable compound must lie in particular below a critical temperature at which the radiation-curable compound undergoes thermal curing.
The critical temperature may easily be determined by means of a calorimetric measurement, i.e., a measurement of the heat absorbed with increasing temperature, in accordance with the above-described determination of the glass transition temperature.
The radiation-curable composition is then extruded directly as the outer layer onto the existing composite or, in the case of coextrusion, is extruded with layers of the composite. Extrusion leads directly to the composite layered sheet or film.
The outer layer is blocking-resistant, i.e., does not adhere, and is radiation-crosslinkable. The composite sheet or film is thermoplastically deformable. If desired, a protective layer (protective film) may be laid down on the outer layer directly following production of the composite sheet or film.
The composite layered sheet or film possesses high gloss and good mechanical properties. Rarely is cracking observed.
The extensibility of the composite layered sheet or film is preferably at least 100%, relative to the unextended state (at 140° C., with a thickness of 30 μm).
The film may be stored without partial curing (as described in DE-A-19 628 966) until subsequent use.
There is very little, if any, sticking or deterioration in performance properties observed up until the time of subsequent use.
The film is used preferably as a coating material.
In this case, a preferred procedure is first to coat the substrates and then to cure the outer layer by means of radiation.
Coating may take place by bonding the film to the substrates. For this purpose, on the reverse of the substrate layer, the film is preferably provided with the adhesive layer E. Suitable substrates include those of wood, plastic or metal.
Coating may also take place by injection backmolding of the film. For this purpose the film is thermoformed, preferably in a thermoforming mold, and the reverse of the substrate layer is injection-backmolded with polymer composition. The polymer composition comprises, for example, polymers which were listed above in the description of the substrate layer or, for example, polyurethane, especially polyurethane foam. The polymers may comprise additives, particular examples including fibers, such as glass fibers, or fillers.
The radiation curing of the outer layer takes place in this case preferably after the thermoforming operation and with particular preference after the injection backmolding of the film.
The radiation cure is effected with high-energy light, e.g., UV light, or electron beams. It may take place at relatively high temperatures. Preference is given here to a temperature above the Tg of the radiation-curable binder.
Where crosslinkers which bring about additional thermal crosslinking, such as isocyanates, have been included too, it is possible to carry out thermal crosslinking by raising the temperature to up to 150° C., preferably up to 130° C., which can be done, for example, simultaneously with or else subsequent to radiation curing.
The films may be used to coat shaped articles. Any desired shaped articles are amenable. With particular preference, the films are used to coat shaped articles where very good surface properties, high weathering stability, and good UV resistance are important. The resulting surfaces are, moreover, highly scratch-resistant and firmly adhering, thereby reliably preventing destruction of the surfaces by scratching or delamination of the surfaces. Accordingly, shaped articles for use outdoors, outside of buildings, constitute a preferred area of application. In particular, the films are used to coat motor vehicle parts, with suitable examples including wings, door trim components, fenders, spoilers, skirts, and exterior mirrors.
426.2 g of isopropylidenedicyclohexanol were dispersed roughly in 566.3 g of hydroxyethyl acrylate at 60° C. with stirring. To this dispersion there were added 1695.2 g of an isocyanurate of hexamethylene diisocyanate, 1.34 g of hydroquinone monomethyl ether, 2.69 g of 1,6-di-tert-butyl-para-cresol and 0.134 g of phenothiazine. Following the addition of 0.538 g of dibutyltin dilaurate, the batch heated up to 93° C. over the course of 20 minutes. After it had been cooled to 75° C., 300 g of acetone were metered in. When the NCO value had dropped to 0.66%, a further 370 g of acetone were added, followed by dropwise addition of 14.87 g of methanol. The mixture was then stirred at 60° C. until the NCO value had fallen to 0. The resin was admixed with an appropriate photoinitiator, applied to a Luran S 797 injection backmolding film, and exposed at 100° C. The pencil hardness of the films was determined in accordance with ASTM D 3363. Pencil hardness of the coated film: 2H
Comparison: pencil hardness of the untreated injection backmolding film (Luran S 797): B
Comparison: pencil hardness of the injection-backmolding protection film (Lucryl G 87): softer than 6B
Two uncured acrylated polyacrylates having different Tg values, and the uncured urethane acrylate, were applied to a Luran S support film and thermoformed at an elevated temperature. After thermoforming, the films were exposed at 100° C.
Hardness of the films:
Urethane acrylate 2H
Binder resin (Tg (before exposure)=46° C.) 3H
Binder resin (Tg (before exposure)=−6° C.) H
First of all, a photoactive mixture was prepared by mixing the following constituents:
Ebecryl ® 40
pentaerythritol triacrylate (UCB)
Ebecryl ® IRR 264
Triacrylate of a tris(2-hydroxy-
ethyl) isocyanurate (UCB)
Ebecryl ® 1290
Aliphatic urethane acrylate (UCB)
Ebecryl ® 5129
Aliphatic urethane acrylate (UCB)
Ebecryl ® 350
Silicone diacrylate (UCB)
Tinuvin ® 292
HALS additive (Ciba SC)
Tinuvin ® 400
UV absorber (Ciba SC)
Irgacure ® 184
Photoinitiator (Ciba SC)
Lucirin ® TPO
The polymethyl methacrylate (PMMA) Lucryl® G 55 was melted at from 190 to 220° C. in an extruder and the photoactive mixture (one part by weight of the mixture to three parts by weight of Lucryl) was metered into the melt at below 170° C. The resulting melt was extruded in the form of a radiation-curable film.
The film obtained was blocking-resistant (i.e., nonadhering) and the resulting composite film was deformable and thermoformable. The radiation-curable outer layer was cured using UV light. (120 W/cm, belt speed 2 to 3 m/min).
The photoactive mixture consisted of:
Aliphatic urethane acrylate (UCB)
Aliphatic triacrylate of a urethane
acrylate in HDDA (UCB)
Photoinitiator (Ciba SC)
HALS additive (Ciba SC)
UV absorber (Ciba SC)
Propoxylated neopentyl glycol
diacrylate (Cray Valley)
Silicone diacrylate (UCB)
Aliphatic UR-Ac (Cray Valley)
Polyethylene glycol diacrylate (Cray
The polyurethane KU-1-8602 (Bayer) was melted at 180 to 220° C. in an extruder and the photoactive mixture (one part by weight to three parts by weight of polyurethane) was metered into the melt at 160° C. The resulting melt was extruded in the form of a radiation-curable film.
The resulting outer layer was blocking-resistant, and the resulting film was deformable and thermoformable.
The radiation-curable outer layer was cured using UV light (120 W/cm, belt speed 2 to 3 m/min).
|Patente citada||Fecha de presentación||Fecha de publicación||Solicitante||Título|
|US4855184 *||2 Feb 1988||8 Ago 1989||Minnesota Mining And Manufacturing Company||Radiation-curable protective coating composition|
|US5387304||15 Mar 1993||7 Feb 1995||Ciba-Geigy Corporation||Application of a painted carrier film to a three-dimensional substrate|
|US5912081||16 Jul 1997||15 Jun 1999||Daimler-Benz Aktiengesellschaft||Method and paint firm for painting an object during a creative shaping|
|US6127039 *||22 Ene 1999||3 Oct 2000||Tdk Corporation||Magnetic recording medium and a process for producing the same|
|US6136882 *||8 Jul 1999||24 Oct 2000||Morton International Inc.||Non-hazing UV curable powder coatings containing crystalline resins|
|US6380279 *||24 Oct 1997||30 Abr 2002||Ucb S.A.||Powder compositions with semicrystalline polyester and amorphous polyester base containing terminal methacryloyl groups|
|US6500545 *||21 Sep 2000||31 Dic 2002||Ppg Industries Ohio, Inc.||Aminoplast-based crosslinkers and powder coating compositions containing such crosslinkers|
|CA2221266A1||9 Dic 1997||10 Jun 1998||Achim Grefenstein||Laminated sheets or films and moldings thereof|
|DE19628966A||Título no disponible|
|DE19651350A1||10 Dic 1996||18 Jun 1998||Basf Ag||Laminated sheet or foil, for moulding e.g. car bodywork|
|DE19654918A1||18 Jul 1996||22 Ene 1998||Daimler Benz Ag||Application of multilayer film coatings universally, e.g. to metal and plastic curved surfaces in car manufacture|
|EP0307918A2||15 Sep 1988||22 Mar 1989||Canon Kabushiki Kaisha||Resin composition curable with an active energy ray containing epoxy resin containing at least a compound having one or more of epoxy group in the molecule|
|EP0361351A2||25 Sep 1989||4 Abr 1990||Ciba-Geigy Ag||Application of a painted film to a three-dimensional object|
|EP0632333A1||25 Ene 1994||4 Ene 1995||Hewlett-Packard Company||Cross-linked polyvinyl butyral binder for organic photoconductor|
|EP0850757A2||23 Dic 1997||1 Jul 1998||Toyo Boseki Kabushiki Kaisha||Laminated polyester film|
|EP0874027A2||23 Abr 1998||28 Oct 1998||Oji Paper Company Limited||Electron beam curable resin composition and composite sheet material produced therefrom|
|Patente citante||Fecha de presentación||Fecha de publicación||Solicitante||Título|
|US7754827 *||13 Jul 2010||Bayer Materialscience Ag||Coated films|
|US7789457||10 Feb 2005||7 Sep 2010||Daimler Ag||Vehicle film component, and method for the production thereof|
|US7857515||15 Jun 2007||28 Dic 2010||S.C. Johnson Home Storage, Inc.||Airtight closure mechanism for a reclosable pouch|
|US7874731||15 Jun 2007||25 Ene 2011||S.C. Johnson Home Storage, Inc.||Valve for a recloseable container|
|US7887238||15 Feb 2011||S.C. Johnson Home Storage, Inc.||Flow channels for a pouch|
|US7935291||13 Jul 2004||3 May 2011||Basf Coatings Ag||Method for producing molded plastic parts having functional surfaces|
|US7946766||24 May 2011||S.C. Johnson & Son, Inc.||Offset closure mechanism for a reclosable pouch|
|US7955538 *||18 Feb 2005||7 Jun 2011||Basf Aktiengesellschaft||Radiation hardened composite layer plate or film|
|US7967509||15 Jun 2007||28 Jun 2011||S.C. Johnson & Son, Inc.||Pouch with a valve|
|US7968199||24 Abr 2006||28 Jun 2011||Basf Coatings Ag||Method for producing films having a coating the films obtained in this way and their use for producing molded parts in particular for use in automobile construction|
|US8231273||17 Dic 2010||31 Jul 2012||S.C. Johnson & Son, Inc.||Flow channel profile and a complementary groove for a pouch|
|US8334052||23 Mar 2011||18 Dic 2012||Basf Aktiengesellschaft||Radiation hardened composite layer plate or film|
|US8613824||6 Dic 2010||24 Dic 2013||Senoplast Klepsch & Co. Gmbh||Multi-layer, substantially polyvinyl chloride- and polyolefin-free composite film|
|US20050008884 *||10 Nov 2003||13 Ene 2005||Johann Kappacher||Multi-layer, substantially polyvinyl chloride- and polyolefin-free composite film|
|US20050124714 *||3 Dic 2004||9 Jun 2005||Bayer Materialscience Ag||Coating compositions|
|US20050221011 *||1 Mar 2005||6 Oct 2005||Basf Aktiengesellschaft||Process for producing semifinished products and moldings|
|US20060198963 *||19 Sep 2005||7 Sep 2006||Dimitry Chernyshov||Process for the production of a coating layer on three-dimensional shaped substrates with radiation-curable coating compositions|
|US20070110905 *||13 Jul 2004||17 May 2007||Horst Hintze-Bruening||Method for producing molded plastic parts having functional surfaces|
|US20070123613 *||22 Nov 2006||31 May 2007||Bayer Materialscience Ag||Coated films|
|US20070166548 *||18 Feb 2005||19 Jul 2007||Basf Aktiengesellschaft||Radiation hardened composite layer plate or film|
|US20080041273 *||28 Nov 2005||21 Feb 2008||Basf Coatings Aktiengesellschaft||Scratchproof, Radiation-Curable Coatings|
|US20080102215 *||19 Dic 2007||1 May 2008||Jan Weikard||Coated films|
|US20080129083 *||10 Feb 2005||5 Jun 2008||Daimlerchrysler Ag||Vehicle Film Component, and Method for the Production Thereof|
|US20080135171 *||25 May 2005||12 Jun 2008||Basf Aktiengesellschaft||Radiation-Hardenable Laminated Plate or Sheet|
|US20080145624 *||29 Oct 2007||19 Jun 2008||Jan Weikard||Printed, moldable films|
|US20080213600 *||24 Abr 2006||4 Sep 2008||Basf Coatings Aktiengesellschaft||Process for Producing Sheets (F) Bearing a Coating (B), the Resultant Sheets (F), and Their Use for Producing Moldings, Especially for Use in the Autombile Construction|
|US20090081448 *||5 Sep 2008||26 Mar 2009||John Jambois||Pultrusion with abrasion resistant finish|
|US20090084574 *||22 Sep 2008||2 Abr 2009||Kim Gene Balfour||Poly(arylene ether) composition and its use in the fabrication of extruded articles and coated wire|
|US20100021737 *||11 Oct 2007||28 Ene 2010||Basf Se||Method of film-coating articles|
|US20110135807 *||6 Dic 2010||9 Jun 2011||Johann Kappacher||Multi-layer, substantially polyvinyl chloride- and polyolefin-free composite film|
|US20120309864 *||14 May 2012||6 Dic 2012||Heraeus Kulzer Gmbh||Denture base material that is fracture-resistant after curing and is obtained from autopolymerizing or cold-polymerizing compositions|
|CN103813903A *||31 Ago 2012||21 May 2014||塞诺桑有限公司||Composite body|
|Clasificación de EE.UU.||428/421, 428/522, 428/518, 428/483, 428/520, 428/482|
|Clasificación internacional||B29K23/00, B29C47/02, B32B38/12, B29C47/06, B32B37/00, B29L31/30, B29C35/08, B32B27/18, B32B27/08, B05D3/06, B29L9/00, B29C45/14, B32B27/32, B32B27/36, B32B27/16, B32B37/15|
|Clasificación cooperativa||Y10T428/31573, Y10T428/3192, Y10T428/31576, Y10T428/31721, Y10T428/31855, Y10T428/31917, Y10T428/31794, Y10T428/31504, Y10T428/31583, Y10T428/31797, Y10T428/3154, Y10T428/31935, Y10T428/31507, Y10T428/31587, Y10T428/31562, Y10T428/31928, Y10T428/31565, B29C47/043, Y10T428/2848, B29C47/0021, B29K2995/0026, B32B27/16, B32B2333/12, B05D3/067, B32B2307/558, B32B2307/412, B32B38/12, B29C47/065, B32B2307/554, B32B2310/0806, B29C45/14811, B29C2035/0827, B32B2605/08, B29C2035/0877, B32B37/153, B32B2038/0076, B32B27/08|
|Clasificación europea||B29C47/06P, B32B27/08, B32B27/16, B29C45/14Q4|
|22 Ene 2002||AS||Assignment|
Owner name: BASF AKTIENGESELLSCHAFT, GERMANY
Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:KOENIGER, RAINER;BECK, ERICH;GREFENSTEIN, ACHIM;AND OTHERS;REEL/FRAME:012491/0749
Effective date: 20000427
Owner name: DAIMLERCHRYSLER AG, GERMANY
Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:KOENIGER, RAINER;BECK, ERICH;GREFENSTEIN, ACHIM;AND OTHERS;REEL/FRAME:012491/0749
Effective date: 20000427
|25 Ene 2008||FPAY||Fee payment|
Year of fee payment: 4
|22 Sep 2011||FPAY||Fee payment|
Year of fee payment: 8
|25 Mar 2016||REMI||Maintenance fee reminder mailed|