|Publication number||US7297407 B2|
|Application number||US 11/230,812|
|Publication date||20 Nov 2007|
|Filing date||19 Sep 2005|
|Priority date||20 Sep 2004|
|Also published as||CN101031419A, EP1802460A1, US7754338, US20060063007, US20070298264, WO2006034346A1|
|Publication number||11230812, 230812, US 7297407 B2, US 7297407B2, US-B2-7297407, US7297407 B2, US7297407B2|
|Inventors||Jerrel C. Anderson|
|Original Assignee||E. I. Du Pont De Nemours And Company|
|Export Citation||BiBTeX, EndNote, RefMan|
|Patent Citations (42), Non-Patent Citations (2), Referenced by (3), Classifications (55), Legal Events (4)|
|External Links: USPTO, USPTO Assignment, Espacenet|
This application claims the benefit of U.S. Provisional Application No. 60/611,596, filed Sep. 20, 2004.
1. Field of the Invention
This invention relates to laminates used in glazing applications. This invention particularly relates to laminates useful as acoustic glazing for sound dampening.
2. Description of the Related Art
Glass laminates having sound-damping properties have found use in architectural applications as well as in vehicles. Such acoustic laminates are desirable to reduce sound transmission from external sources to the interior of a building or an automobile, for example.
Plasticized polyvinyl butyral (PVB) sheet is used in the manufacture of transparent laminate structures such as, for example: windshields for vehicles including automobiles, motorcycles, boats and airplanes, windows in buildings such as office buildings, apartment buildings, houses, and/or commercial buildings, for example.
In modern vehicles—particularly in trains, planes and automobiles—passenger comfort has become an important selling point in commercial transactions involving same. One important feature in a modern vehicle is the ability to minimize noise that originates from outside of the passenger compartment of the vehicle. Automobiles are particularly targeted for improving the acoustic quality of the passenger's ride. Noises coming from the engine compartment, from the sound of tires rolling across a road or the ground, and wind noise created as a car moves at rapid speed through air are all contributors to the noise generated as a car is used as it was intended.
Various improvements and modifications have been made to cars in order to improve the quietness of a passenger's travel. However, one major source of noise is sound that passes through the windows of a vehicle. The windows of a car are typically good conductors of sound waves—particularly at critical sound frequencies, that is, at sound frequencies that are perceptible to the human ear. Moreover, sound reduction in office and other buildings from noise emanating from outside of the building can be desirable in settings where outside noises can reach the level of distraction inside of a building.
Various patents describe inventive attempts to address the problem of noise reduction in vehicles and/or in buildings. U.S. Pat. No. 5,368,917 and U.S. Pat. No. 5,478,615 describe acoustic laminated glazings for vehicles comprising conventional polyvinyl butyral (PVB). U.S. Pat. No. 6,132,882 describes a sound-damping laminate comprising a vibration-damping layer such as a polyacrylate, at least one flexible plastic layer such as PVB, and a rigid glass or plastic sheet. U.S. Pat. No. 5,773,102 describes a soundproofing laminated glass pane wherein a high-performance acoustic film is combined with at least one film having ordinary acoustic performance, such as PVB. U.S. Pat. No. 5,190,826 describes interlayers for use in sound-insulating laminated glass. U.S. Pat. No. 6,074,732 describes a soundproofing laminated window made of two glass sheets between which are polymer layers in the order of PVB/PET/acrylate/PET/PVB. The PVB layers are conventional (that is, non-acoustic) PVB. U.S. Pat. No. 6,432,522 describes transparent laminates having sound attenuation properties comprising an interlayer film having at least two layers. WO 01/19747 A1 describes glass laminates wherein PVB is softened (plasticized) with 20 to 50 wt % of a two-component plasticizer mixture comprising 30 to 70 wt % of a polyalkylene glycol as one of the components. However, impact resistance of a laminate using softened PVB can be detrimentally affected.
Use of ethylene acid copolymers or salts thereof produce rigid interlayers which can be particularly useful as threat-resistant glazing units in automobiles and buildings. Imparting sound-dampening properties to such interlayers can be difficult because of the rigidity of these materials, and relative lack of adhesion to other interlayer materials with known acoustic properties such as, for example, PVB.
It can be desirable to have a laminate with sound dampening (sound-damping) properties that retains its impact resistance and resistance to penetration. It can be particularly desirable to have such properties in a threat-resistant glazing unit.
In one aspect the present invention is a sound-damping laminate article comprising: at least 3-layers of composite interlayer, wherein one layer of the composite interlayer is a polyester (PET) polymer positioned between two dis-similar polymer layers, and wherein the dis-similar polymers are polymers selected from the group consisting of: polyvinylbutyrals (PVB); ionoplast resins (ionomers); polyurethanes (PU); polyvinyl chlorides; polycarbonates; polyacetals; ethylene acid copolymers, including ethylene acid terpolymers (acid copolymers); and polyolefins, including polyethylenes and polypropylenes.
In one embodiment, the present invention is a laminate having sound-dampening properties. A laminate of the present invention has sound-damping properties in the frequency range of from about 10 Hz to about 10,000 Hz at a temperature in the range of from about 10° C. to about 30° C. A laminate of the present invention comprises a multilayer composite interlayer which comprises at least three polymer layers. Preferably the composite interlayer imparts to the laminate sound-damping properties in the range of from about 1,000 Hz to about 5,000 Hz at a temperature in the range of from about 10° C. to about 30° C. More preferably, the interlayer provides the above sound-damping properties at a temperature in the range of from about 15° C. to about 25° C.
Sound-damping, as the term is used in the present application, refers to the sound loss that occurs on the transmission of sound from an incident surface of a laminate (the surface exposed to a sound wave) to an interior surface of the laminate (the side opposite the incident surface). Individual laminate glazing constructions have a loss factor and an equivalent bending rigidity modulus that can be determined for each construction, and which can be related to Sound Transmission Loss for the glazing. Laminate glazing constructions of the present invention comprise three-layer interlayer laminate constructions having loss factors greater than about 0.05, measured at 20° C. by the method described herein throughout the range of from 50 to 10000 Hz. Preferably, laminates of the present invention have loss factors of at least about 0.08 throughout the range of from 50 to 10000 Hz, and more preferably the loss factor is at least about 0.15 throughout the range of from 50 to 10000 Hz.
In the practice of the present invention, an equivalent bending rigidity modulus can be determined to provide Sound Transmission Loss of the laminate glazing of the present invention.
A sound-damping laminate of the present invention comprises, or consists essentially of, a polyester (PET) layer positioned between at least two other polymeric interlayers that are chemically distinct from the PET layer such that the laminate structure can be described as comprising the structure: polymer 1/PET/polymer 2. Polymer 1 and polymer 2 can either be the same or can be different materials. While there is no strict order to the laminate construction of the composite interlayer, it can be preferred to position the PET layer directly between the at least two other layers such that polymer 1 and polymer 2 each contact opposite surfaces of the intervening PET layer. Other laminate structures can be envisioned utilizing multiple layers of any of the layers, or combining chemically distinct interlayers described herein in any combination that can provide the desirable acoustic effect. It is particularly preferred that the laminate have adhesion between the that is suitable for placing the laminate into typical glazing applications. Suitable adhesion can be inherent between the polymer layers, or can be the result of a process treatment, or a coating on at least one surface of the layers.
In one embodiment, the PET layer can be flame-treated to enhance adhesion to a dissimilar polymer layer. In a particularly preferred embodiment, the PET layer has a coating of a polyallylamine-based primer applied to at least one of its surfaces, preferably to both surfaces of the PET. PET coated with primer as described herein can provide a means for laminating two dissimilar polymeric interlayers that otherwise cannot be laminated conventionally. The primer and its application to the PET polymeric layer are described in U.S. Pat. Nos. 5,411,845; 5,770,312; 5,690,994; and 5,698,329. Generally, the PET film is extruded and cast as a film by conventional methods, and the polyallylamine coating is applied to the PET film either (i) before stretching or (ii) between the machine direction stretching and transverse direction stretching operations, and/or after the two stretching operations and heat setting in the stenter oven. It is preferable that the coating be applied before the transverse stretching operation so that the coated PET web is heated under restraint to a temperature of about 220° C. in the stenter oven in order to cure the polyallylamine to the PET surface. In addition to this cured coating, an additional polyallylamine coating can be applied on it after the stretching and stenter oven heat setting in order to obtain a thicker overall coating. The coated PET treated in this general manner is the primer (PRIMER) used herein to enhance the adhesion between dissimilar polymeric layers in a laminate construction. The coated PET layer can be required, for example, in producing a laminate construction wherein polymer 1 and polymer 2 referenced hereinabove are selected from ionomeric copolymers and polyvinylbutyrals. PVB and ionoplast interlayers do not normally adhere to each other satisfactorily without, for example, flame treatment of an intermediary adhesive layer.
Adhesive strength in a laminate of the present invention is determined by the 90° peel test. The adhesive strength between dissimilar polymer layers in the present invention can be about zero (0) to about less than 10 lb/inch without any treatment to enhance adhesion, and with flame treatment the adhesive strength can be improved to about 10 lb/inch. Using a PRIMER as described herein can improve the peel strength to at least about 10 lb/in, and preferably to at least 15 lb/inch. Peel strength can give indication of the integrity of the multilayer laminate, and high peel strength can be an indicator of good resistance to delamination in the fully constructed laminate.
Suitable polymers useful in a laminate of the present invention include, for example: PET; PVB (standard non-acoustic PVB and/or “acoustic” PVB wherein acoustic PVB is highly plasticized PVB, as described herein); ionoplast resins, which are ethylene acid copolymer ionomers (that is, at least partially neutralized acid copolymers); ethylene vinyl acetates (EVA); polyurethanes; polyvinyl chlorides; polycarbonates; polyacetals; ethylene acid copolymers (which are inclusive of ethylene acid terpolymers); polyolefins, including polyethylenes and polypropylenes. Preferred for use herein are polymers that are transparent, or that can be made to be transparent, such that they are suitable for use in glazing end-use applications. Particularly preferred for use herein are PET, PVB, and ionoplast resins.
Non-acoustic PVB is a commercially available product that can be obtained from E.I. DuPont de Nemours and Company (DuPont) under the tradename of Butacite®. Ionoplast resins suitable for use herein are copolymers (inclusive of terpolymers) of ethylene and unsaturated carboxylic acids wherein at least a portion of the acid groups in the copolymer have been neutralized to the salt form of the acid. Extruded sheets of ionoplast resin suitable for use in the present invention can be obtained from DuPont under the trade name of SentryGlas® Plus (SGP).
Polyester films (PET) are well-known polymer films that can also be obtained commercially. PET suitable for use herein can additionally comprise a hardcoat such as an abrasion resistant polysiloxane material or an oligomeric coating as described in U.S. application Ser. No. 10/925,842 (published as US 2005-0077002 A 1 on Apr. 14, 2005) on one of its surfaces. The polysiloxane coated PET can be obtained commercially from DuPont. In laminates of PET and other polymers such as PVB and SGP, it can be conventional to enhance the adhesion of the PET to the other polymers by some treatment step such as a flame treatment. In the practice of the present invention, adhesion of PET to any of the other polymers can be improved by either flame treating the PET or by applying PRIMER to either surface of the dissimilar polymers prior to laminating the layers using conventional laminating methods. Use of the PRIMER to improve the adhesion of PET to PVB can eliminate the need for a flame treatment to obtain suitable adhesion between these polymers.
In one embodiment, the PET can be used to adhere stiff PVB having a low plasticizer content (less than 15 pph parts)—and thus higher modulus—to “normal” PVB and/or to other polymeric interlayer materials as defined herein.
In a particularly preferred embodiment the sound-damping laminate of the present invention comprises at least one layer of a sound-damping (acoustic) PVB that is highly plasticized with at Least one plasticizer or a mixture of plasticizers. In this embodiment the plasticizer is included in an amount of from about 40 parts per hundred (pph) to about 50 pph parts PVB. Preferably, the interlayer is plasticized with from about 41 pph to about 49 pph, more preferably from about 42 pph to about 49 pph. and most preferably from about 44 to about 47 pph. In a much preferred embodiment, the sound-damping PYB is highly plasticized with one plasticizer. PVB useful in the practice of the present invention is described in U.S. application Ser. No. 10/519,661, fully incorporated herein by reference (published as US 2005-0288429 A 1 on Dec. 29, 2005).
Sound-damping (acoustic) PVB as used in the practice of the present invention can be used in any thickness that provides the desired acoustic effect when combined with the other components of the laminate. Preferably, however, the PVB used has a thickness in the range of from about 15 mils to about 90 mils. More preferably, the sound-damping PVB has a thickness in the range of from about 1 mil to about 60 mils, and even more preferably in the range of from about 10 mils to about 40 mils. Most preferably, the thickness of the sound-damping PVB is in the range of from about 15 mils to about 40 mils. Multiple PVB sheets of various thicknesses can be stacked to obtain a sound-damping PVB stack having a desirable thickness.
Plasticizer suitable for use in the practice of the present invention is any plasticizer that is used conventionally with PVB. For example, conventional plasticizers useful in the preparation of plasticized PVB include such plasticizers as: diesters of polyethylene glycol such as triethylene glycol di(2-ethylhexanoate) (3GO), tetraethylene glycol di-heptanoate (4G7), triethyleneglycol di(2-ethylbutyrate), and di-hexyl adipate. Most preferred for use in highly plasticized PVB is 4G7.
Preferably, the plasticizer is one that is compatible (that is, forms a single phase with the interlayer) in the amounts described hereinabove, with regard to acoustic PVB, with PVB having a hydroxyl number (OH number) of from about 17 to about 23. Preferably the PVB of the present invention has an OH number of from about 18 to about 21, more preferably the OH number is from about 18 to about 19.5, and most preferably from about 18 to about 19. A particularly preferred plasticizer for use in the practice of the present invention is one which is compatible with the PVB in any of the preferred ranges for hydroxyl number.
Generally, laminates of the present invention can be useful in architectural as well as in vehicular applications. For example, the laminates of the present invention can be useful as: windows in buildings; doors; partitions; hurricane windows; bullet-resistant glazings; sidelites, moonroofs, sunroofs and windshields in automobiles; windows in planes and trains; and other applications where sound-dampening laminated glazings can be desirable.
Acoustic laminates of the present invention can be combined with decorative interlayers to produce glazings that reduce sound transmission in addition to incorporating designs, graphics, colors, or other decorative images.
The Examples and Comparative Examples are presented for illustrative purposes only, and are not intended to limit the scope of the present invention in any manner that is inconsistent with the teachings provided of the specification.
Laminates having the structures given below were made using an autoclave cycle of 135° C. at 200 psi for 30 minutes using a conventional vacuum bagging process.
Loss Factor (η) Determination
Loss factor is determined from the measurement of the input impedence of a glass beam sample. A glass laminate specimen (25 mm×300 mm) is placed at its center onto an impact button (15 mm diameter), and affixed thereto with a cyanoacrylic glue. The impact button is supported on an impedence head, which is used to inject a measured force into the specimen via the impact button. A white noise type force between 0 and 5000 Hz is used to inject the specimen. The loss factor is then calculated using the formula:
η=Δfi /f resi,
where Δfi is the frequency difference between the frequencies on the resonance curve (fresi) having an impedence of 3 dB less than the maximum impedence. The specimen held in an environmental chamber at the desired set temperature before and during the determination. The impedence head is connected to a dash pot, which is connected to a power amplifier, which is connected to a noise generator. The impedence is measured by a FFT analyzer/computer set-up. A detailed description of the method and apparatus are described in ISO/PDPAS 16940 (published Jul. 16, 2002): “Glass in Building—Glazing and Airborne Sound Insulation—Measurement of the Mechanical Impedance of Laminated Glass”, herein incorporated by reference.
GLASS/ionomer/PET/PVB/GLASS laminates were prepared using PET coated on both sides with a polyallylamine primer coating. Laminated to opposite surfaces of the PET were one sheet each of 30 mil thick PVB interlayer (BE-1028 Butacite®, available from DuPont) and 60 mil thick SentryGlas®) Plus ionoplast interlayer (available from DuPont). The PET sheet was 6.5-7.0 mils thick. The loss factor was calculated and is reported in Table 1.
The procedure of Example 1 was followed with the exception that the laminate of this example included two layers of ionomer interlayer with the PET layer. The loss factor was calculated and is reported in Table 1.
A laminate having a structure Glass/90 mil ionomer/Glass was constructed and measured for loss factor. The results are reported in Table 1.
A laminate having a structure Glass/90 mil PVB/Glass was constructed and measured for loss factor. The results are reported in Table 1.
A laminate having a structure Glass/90 mil acoustic PVB/Glass was constructed and measured for loss factor. The results are reported in Table 1.
The procedure of Example 1 was followed with the exception that a laminate having the structure Glass/60 mil ionomer/PET/40 mil acoustic PVB/Glass was constructed and measured for loss factor. The results are reported in Table 1.
The procedure of Example 2 was followed with the exception that a laminate having the structure Glass/60 mil ionomer/PET/30 mil acoustic PVB/Glass was constructed and measured for loss factor. The results are reported in Table 1.
The procedure of Example 3 was followed with the exception that a laminate having the structure Glass/60 mil PVB/PET/30 mil PVB/Glass was constructed and measured for loss factor. The results are reported in Table 1.
The procedure of Example 4 was followed with the exception that a laminate having the structure Glass/60 mil acoustic PVB/PET/30 mil acoustic PVB/Glass was constructed and measured for loss factor. The results are reported in Table 1.
The procedure of Example 5 was followed with the exception that a laminate having the structure Glass/60 mil PVB/PET/30 mil acoustic PVB/Glass was constructed and measured for loss factor. The results are reported in Table 1.
The procedure of Example 6 was followed with the exception that a laminate having the structure Glass/60 mil colored PVB/PET/40 mil acoustic PVB/Glass was constructed and measured for loss factor. The results are reported in Table 1.
A laminate having a structure Glass/40 mil acoustic PVB/Glass was constructed and measured for loss factor. The results are reported in Table 1.
A laminate having a structure Glass/30 mil acoustic PVB/Glass was constructed and measured for loss factor. The results are reported in Table 1.
Loss Factor (20° C.) @ Frequency (Hz)
|Cited Patent||Filing date||Publication date||Applicant||Title|
|US3816201 *||22 Feb 1973||11 Jun 1974||Sierracin Corp||Laminated structures and method of forming the same|
|US4059469 *||5 Jan 1976||22 Nov 1977||Libbey-Owens-Ford Company||Glazing units, methods of making the same and adhesion promoters therefor|
|US4614676||1 Jul 1983||30 Sep 1986||Saint-Gobain Vitrage||Multiple window glass having thermal and acoustical insulating properties|
|US4619973 *||17 Aug 1984||28 Oct 1986||Advanced Glass Systems, Inc.||Ionomer resin films|
|US4663228 *||17 Dec 1985||5 May 1987||Advanced Glass Systems Corp.||Laminated safety glass|
|US4742107||6 May 1987||3 May 1988||E. I. Du Pont De Nemours And Company||Noise reduction and damping compositions|
|US5002820 *||25 May 1989||26 Mar 1991||Artistic Glass Products||Laminated safety glass|
|US5190826||13 May 1991||2 Mar 1993||Sekisui Chemical Co., Ltd.||Interlayers for use in sound-insulating laminated glasses|
|US5368917||4 Nov 1993||29 Nov 1994||Saint Gobain Vitrage International||Acoustic protective glazing for a vehicle|
|US5411845||4 Aug 1994||2 May 1995||Imperial Chemical Industries Plc||Polymeric film coated with a subbing layer containing cross-linking agent and (N-substituted) monoallylamine polymer|
|US5415942||4 Nov 1993||16 May 1995||E. I. Du Pont De Nemours And Company||Glass/plastic laminate structures for glazing applications|
|US5427842 *||27 May 1994||27 Jun 1995||Minnesota Mining And Manufacturing Company||Tear resistant multilayer films and articles incorporating such films|
|US5478615||6 Sep 1994||26 Dec 1995||Saint Gobain Vitrage International||Acoustic protective glazing for a vehicle|
|US5690994 *||5 Jun 1995||25 Nov 1997||Imperial Chemical Industries Plc||Polymetric film|
|US5698329 *||5 Jun 1995||16 Dec 1997||Imperial Chemical Industries Plc||Polymeric film|
|US5770312 *||9 Jun 1994||23 Jun 1998||Imperial Chemical Industries Plc||Polymeric film|
|US5773102 *||16 Sep 1996||30 Jun 1998||Saint-Gobain Vitrage, S.A.||Soundproofing laminated glass pane|
|US5796055 *||13 Jan 1997||18 Aug 1998||Ppg Industries, Inc.||Sound absorbing article and method of making same|
|US5979932 *||13 Aug 1997||9 Nov 1999||Saint-Gobain Vitrage||Protection for the occupants of a vehicle in the event of a side impact|
|US6074732||25 Nov 1997||13 Jun 2000||Saint Gobain Vitrage||Soundproofing laminated window for vehicles|
|US6074932 *||28 Jan 1998||13 Jun 2000||Texas Instruments - Acer Incorporated||Method for forming a stress-free shallow trench isolation|
|US6119807||26 May 1998||19 Sep 2000||Ppg Industries Ohio, Inc.||Sound absorbing article and method of making same|
|US6132882 *||16 Dec 1996||17 Oct 2000||3M Innovative Properties Company||Damped glass and plastic laminates|
|US6352754 *||23 Apr 1998||5 Mar 2002||Saint-Gobain Glass France||Method for making a laminated glass sheet|
|US6432522 *||9 Jun 1999||13 Aug 2002||Saint-Gobain Vitrage||Transparent acoustical and mechanical barrier|
|US6436219 *||6 Aug 1997||20 Aug 2002||Dupont Teijin Films U.S. Limited Partner||Polyester film|
|US6903152 *||2 Mar 2001||7 Jun 2005||Sekisui Chemical Co., Ltd.||Interlayer film for laminated glass and laminated glass|
|US20010046595 *||14 Dec 2000||29 Nov 2001||Moran James R.||Intrusion resistant glass laminates|
|US20020006504||3 May 2001||17 Jan 2002||Saint-Gobain Glass France||Laminated glazing material|
|US20030054160 *||16 May 2002||20 Mar 2003||Fisher W. Keith||Infrared absorbing compositions and laminates|
|US20050077002 *||25 Aug 2004||14 Apr 2005||Anderson Jerrel C.||Mar-resistant oligomeric-based coatings for glass-plastic glazing products|
|US20050089692||28 Oct 2003||28 Apr 2005||Anderson Jerrel C.||Ionomer resins as interlayers for use with imbedded or attached IR reflective or absorptive films in laminated glazing applications|
|US20050129954 *||12 Dec 2003||16 Jun 2005||Anderson Jerrel C.||Use of PET film primed with polyallylamine coatings in laminated glass glazing constructions|
|US20050288429||4 Aug 2003||29 Dec 2005||Eli Lilly And Company||Process for controlling polyvinylbutyral physical properties by controlling stereochemistry of same|
|US20060008648||29 Oct 2003||12 Jan 2006||Bennison Stephen J||Polyvinylbutyral interlayers having superior acoustical properties and method of preparing same|
|US20060070694||22 Nov 2005||6 Apr 2006||Saint-Gobain Glass France||Laminated glazing material|
|US20060182983||31 Oct 2005||17 Aug 2006||Paul John W||Thermoplastic resin compositions suitable for use in transparent laminates|
|US20060210776||17 Mar 2005||21 Sep 2006||Solutia, Inc.||Sound reducing wedge shaped polymer interlayers|
|US20060210782||17 Mar 2005||21 Sep 2006||Solutia, Inc.||Sound reducing polymer interlayers|
|EP0852999A2||7 Jan 1998||15 Jul 1998||Ppg Industries, Inc.||Sound absorbing article and method of making same|
|WO2001019747A1||16 Aug 2000||22 Mar 2001||Ht Troplast Ag||Compound safety glass and pvb foil for the production thereof|
|WO2005058598A1||10 Dec 2004||30 Jun 2005||E.I. Dupont De Nemours And Company||Use of pet film primed with polyallylamine coatings in laminated glass glazing constructions|
|1||International Preliminary Report on Patentability for PCT/US2005/033834, dated Aug. 8, 2006.|
|2||PCT International Search Report, International Application No. PCT/US2005/033834, Dated Sep. 20, 2005.|
|Citing Patent||Filing date||Publication date||Applicant||Title|
|US20090297806 *||21 Apr 2009||3 Dec 2009||David Francis Dawson-Elli||Glass laminated articles and layered articles|
|US20120070642 *||22 Nov 2011||22 Mar 2012||E.I. Du Pont De Nemours And Company||Safety glazings with improved weatherability|
|WO2015126709A1||12 Feb 2015||27 Aug 2015||3M Innovative Properties Company||Multi-layer cover tape constructions with graphite coatings|
|U.S. Classification||428/441, 428/442, 428/355.00R, 428/480, 428/426, 428/430, 428/483|
|International Classification||B32B17/06, B32B17/10, B32B27/36, B32B27/08, B32B27/30|
|Cooperative Classification||Y10T428/31938, Y10T428/31565, Y10T428/31935, Y10T428/31786, Y10T428/31649, Y10T428/31797, Y10T428/31551, Y10T428/31616, Y10T428/31736, Y10T428/31507, Y10T428/31645, Y10T428/31855, B32B2255/10, B32B17/10761, Y10T428/2852, B32B27/30, B32B27/36, B32B17/10036, B32B2605/08, B32B17/1055, B32B2419/00, B32B2250/03, B32B27/22, B32B17/10743, G10K11/168, B29C55/023, B32B27/08, B32B2255/24, B32B2307/102, B32B17/10, B32B2605/006, B32B2250/24|
|European Classification||B32B17/10, B32B27/22, G10K11/168, B32B17/10G, B32B27/36, B29C55/02B, B32B27/08, B32B27/30, B32B17/10G28, B32B17/10G24, B32B17/10C4|
|12 Apr 2006||AS||Assignment|
Owner name: E. I. DU PONT DE NEMOURS AND COMPANY, DELAWARE
Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:ANDERSON, JERREL C.;REEL/FRAME:017461/0894
Effective date: 20050916
|1 Jul 2008||CC||Certificate of correction|
|20 Apr 2011||FPAY||Fee payment|
Year of fee payment: 4
|6 May 2015||FPAY||Fee payment|
Year of fee payment: 8