|Publication number||US8093593 B2|
|Application number||US 11/516,616|
|Publication date||Jan 10, 2012|
|Filing date||Sep 7, 2006|
|Priority date||Dec 21, 2001|
|Also published as||US7109069, US20030234395, US20070001228, US20120097963|
|Publication number||11516616, 516616, US 8093593 B2, US 8093593B2, US-B2-8093593, US8093593 B2, US8093593B2|
|Inventors||Chiho Kokubo, Aiko Shiga, Shunpei Yamazaki, Hidekazu Miyairi, Koji Dairiki, Koichiro Tanaka|
|Original Assignee||Semiconductor Energy Laboratory Co., Ltd.|
|Export Citation||BiBTeX, EndNote, RefMan|
|Patent Citations (76), Non-Patent Citations (4), Referenced by (2), Classifications (30), Legal Events (1)|
|External Links: USPTO, USPTO Assignment, Espacenet|
1. Field of the Invention
The present invention relates to a semiconductor device using a crystalline semiconductor film crystallized by radiating an amorphous semiconductor film with a laser beam and a method of manufacturing the same.
2. Description of the Related Art
There has been a known technology for crystallizing an amorphous semiconductor film formed on a substrate such as glass by means of a laser process. The laser process means a method of recrystallizing a damaged or amorphous film formed on a semiconductor substrate or a semiconductor film, a method of crystallizing an amorphous semiconductor film formed on an insulating surface or a method of improving crystallinity of a semiconductor film (crystalline semiconductor film) having a crystalline structure. A gas laser represented by an excimer laser or a solid laser represented by a YGA laser is usually used as a laser oscillator device used for the laser process.
A feature of using a laser beam is in that a laser beam is used for radiation and an area absorbing an energy of the laser beam can only be heated selectively, different from a case of a heating process using radiating heating or conducting heating. For example, in a laser process using an excimer laser oscillator device, a process of crystallization or activation of a semiconductor film is achieved by heating a semiconductor film selectively and locally with almost no heat-damage to a glass substrate.
As an example of the laser process, there is a known method of processing a beam linearly by means of an optical system to use the beam for radiation like a laser processing device disclosed in Japanese Patent Laid-Open No. 8-195357. Further, a method of crystallization with a solid laser oscillator device such as an Nd:YVO4 laser is disclosed in Japanese Patent Laid-Open No. 2001-144027. This document discloses that the second higher harmonic of a laser beam used for radiation from the solid laser oscillator device allows the crystalline semiconductor film to have a larger grain size than conventional cases.
Especially, application to a thin film transistor (hereinafter referred to as a TFT) in a method of crystallization using a continuous wave solid laser oscillator device is reported in “Ultra-high Performance Poly-Si TFTs on a Glass by a Stable Scanning CW laser Lateral Crystallization”, A. Hara, F. Takeuchi, M. Takei, K. Yoshino, K. Suga and N. Sasaki, AMLCD '01 Tech. Dig., 2001, pp. 227-230. This document discloses an example of a method of producing a TFT with a polycrystalline silicon film crystallized by means of the second higher harmonic of a solid continuous oscillator laser (YVO4) for diode excitation.
When a continuous wave laser beam is used for radiation to crystallize an amorphous semiconductor film formed on an insulating surface, a crystal having a comparatively large grain size can be formed even on a glass substrate. It has not been possible, however, to orient all surfaces of a substrate to a particular single crystal orientation.
Almost all part of crystallization of an amorphous semiconductor film by means of a laser beam grows through a melt-solidification process regardless of pulse oscillation or continuous wave. In further detail, there are two stages considered: a stage of producing a crystal core; and a stage of crystal growth from the core. In most conventional methods, however, it is not possible to control producing position and density of a crystal core, so that crystallization has been performed by means of a naturally produced crystal core. Therefore, there is a problem that a crystal cannot be grown with a particular orientation. Consequently, grains of crystal are formed in any positions in a plane of a glass substrate and are in only small size such as around 0.2 to 0.5 μm.
Usually, a large number of defects are produced in a grain boundary. The defects are considered to be a factor confining mobility of field effect of a TFT. Moreover, the crystal orientation is random due to dependence on a crystal core produced at any time, so that the crystalline semiconductor cannot be oriented in a line.
In a laser process using a pulse width oscillation laser oscillator device, crystal growth caused by a crystal core is dominant, and thereby, a grain size cannot be enlarged in practice. Concretely, it is impossible to form a crystal in a channel forming area of a TFT, the crystal not existing in a grain boundary and being possible to be considered a substantially single crystal in a view of element level. Not only a grain boundary but also a defect or displacement produced is caused by contraction of a volume of a film due to thickening in accordance with crystallization.
On the other hand, a method of crystallization with a continuous wave laser beam scanning to perform melt-solidification is regarded as a method close to a zone melting method in which continuous crystal growth allows a grain size to be enlarged. There is, however, a problem that quality of a crystal to be obtained depends on crystallinity in a range, which is a first seed of crystallization. Concretely, crystal growth expects a crystal core accidentally produced.
As described above, in a conventional method of crystallization using a laser beam, variance (or dispersion) in a TFT characteristic becomes large, which causes various functions of a semiconductor device comprising TFTs as components of its electronic circuit to be restrained.
In view of the above problems, an object of the invention is to improve crystallinity of a crystalline semiconductor film formed by crystallizing an amorphous semiconductor film so as to provide a TFT capable of operating at higher speed.
In order to solve the above problem, according to the invention, a first shape of semiconductor region is formed in an island configuration on an insulating surface to be crystallized by means of a continuous wave laser beam, and then, a second shape of semiconductor region is formed so that an inner part of the first shape of semiconductor region would be used for an active layer such as a TFT. For the purpose of reducing dispersion of a characteristic of an element produced by means of a crystalline semiconductor film, the crystallinity of an active region decisive for the characteristic of the element should be homogenized. The invention, therefore, devised a configuration of a region, which would be an origin of crystallization in the first shape of semiconductor region.
Concretely, a first shape of semiconductor region having on its one side a plurality of sharp convex top-end portions (projections) is formed first and a continuous wave laser beam is used for radiation from the above region so as to crystallize or improve crystallinity of the first shape of semiconductor region along a scanning direction of the laser beam. Preferably, a continuous wave laser beam condensed in one or plural lines on a radiation surface is used for the laser beam. Then, the first shape of semiconductor region is etched to form on its inner side a second shape of semiconductor region on which a channel forming region and a source and drain region are formed. The second shape of semiconductor region has a plurality of oblong semiconductor regions so that a channel forming range would be formed on respective crystal regions extending from the plurality of convex end portions, and is etching-processed by means of a photoetching method so that a semiconductor region adjacent to the channel forming region would be eliminated. That is to say, a first shape of semiconductor region in which a plurality of semiconductor regions having on its one side a sharp convex top-end portion is disposed in parallel is formed from a semiconductor film formed on an insulating surface, and a continuous wave laser beam is used for radiation from the above first shape of semiconductor region so as to crystallize or improve crystallinity of the first shape of semiconductor region along a scanning route of the laser beam.
The continuous wave laser beam to be condensed in a line preferably has strength distribution in which an energy density distribution is even in a longitudinal direction. In a lateral direction, any distribution such as Gauss distribution, for example, is available. In a laser process, scanning is performed in a direction crossing the longitudinal direction of a continuous wave laser beam to be condensed in a line. This allows crystals to grow extending in parallel to the scanning direction since the strength distribution is even in a longitudinal direction. Namely, energy density distribution uneven in a longitudinal direction causes temperature inclination, so that crystals extend in accordance with the inclination or disordered crystals would be formed.
It is possible to use a rectangular beam solid laser oscillator device as a light source of a continuous wave laser beam, and typically, to employ a slab laser oscillator device.
Intervals between adjacent oblong semiconductor regions in the second shape of semiconductor regions are preferably twice or more the length in a channel width direction of the above semiconductor region and 0.5 to 1.0 μm in view of crystal growth. In this oblong semiconductor region, a low density drain region and electrodes to which common potential is applied through an insulating film is formed to provide a channel forming region.
Thus, a TFT provided in a second shape of semiconductor region formed after a first shape of semiconductor region is crystallized or improved in crystallinity has a crystalline semiconductor film integrally formed with a plurality of rectangular semiconductor regions provided in parallel and a crystalline semiconductor film integrally formed with a pair of semiconductor regions connected to the above rectangular semiconductor region. In the plurality of rectangular semiconductor regions, a channel forming region is formed with electrodes crossing through an insulating film and crystals extend along a direction of the channel length.
Otherwise, the TFT provided with a second shape of semiconductor region has a crystalline semiconductor film integrally formed with a semiconductor region in which a plurality of rectangular semiconductor regions provided in parallel are connected in series and a pair of semiconductor regions connected to both ends of the rectangular semiconductor region. In the plurality of rectangular semiconductor regions, a channel forming region is formed with electrodes crossing through an insulating film and crystals are provided extending along a direction of the channel length.
Crystals in the rectangular semiconductor region provided with a channel forming region extend parallel to the channel length direction and is characterized in that the crystal orientation aligns. Each of the plurality of rectangular semiconductor regions is provided with an interval twice or more the length in the channel width direction thereof.
That is, a region provided with a channel forming area for a TFT in a second shape of semiconductor region is provided so as to be formed with good crystals extending from a plurality of sharp convex top-end portions in one end portion of the first shape of semiconductor region. Alternatively, the region provided with a channel forming area is partly etched to in order to prevent a grain boundary extended from the concave portion or a distortion-accumulated crystal from overlapping a channel forming region.
In accordance with such a structure, a plurality of rectangular semiconductor regions are provided in parallel to form a transistor, so that dispersion of a characteristic between elements can be made small. Further, using only good crystals can improve mobility of field effect.
The word of an amorphous semiconductor film according to the invention is used in a narrow sense and means not only a semiconductor film having a completely amorphous structure but also a so-called microcrystalline semiconductor film which contains microcrystalline grains and a semiconductor film locally including a crystalline structure. An amorphous silicon film is used typically, as well as an amorphous silicon germanium film and an amorphous silicon carbide film.
Other features and advantages of the present invention will appear more clearly upon reading the following detailed description, made with reference to the annexed drawings in which:
Now a mode for carrying out the invention will be described with reference to drawings. A perspective view of
A mask pattern is formed on the amorphous semiconductor film 103 to form a first shape of semiconductor region 104 as shown in
The first shape of semiconductor region 104 can have any outline as long as it is provided in a region 105 at its end with a plurality of sharp convex top-end portions. An angle of the convex top-end portion is preferably 90 degrees±30 degrees.
Scanning is performed by means of a continuous wave laser beam 106 in a single direction from the region 105 at one end of the first semiconductor region 104 toward the other end (a direction shown by an arrow in the drawing) to cause crystallization. It is also possible to carry out return scanning in a direction reverse to the original scanning. A laser beam to be used may preferably have strength dispersion such that there is an even region in a longitudinal direction while it disperses in a lateral direction. As a laser oscillator device used for a light source, employed a rectangular beam solid laser oscillator device, most preferably, a slab laser oscillator device. Alternatively, it is possible to employ a solid laser oscillator device using a crystal, which consists of a crystal such as YAG, YVO4, YLF and YAlO3 doped with Nd, Tm or Ho, in combination with a slab structure amplifier.
As slab materials, may be used a crystal such as Nd:YAG, Nd:GGG (gadolinium gallium garnet) and Nd:GSGG (gadolinium scandium gallium garnet). A laser beam progresses through the plate-shaped laser medium in a zigzag light path, repeating total reflection.
A wavelength of a continuous wave laser beam is preferably 400 to 700 nm in view of an optical absorption coefficient of an amorphous semiconductor film. A light in such a waveband can be obtained by taking second and third harmonics of a fundamental wave by means of a wavelength converting element. As the wavelength converting element, may be used ADP (ammonium dihydrogenphosphate), Ba2Nanb5O15 (barium sodium niobate), CdSe (cadmium selenide), KDP (potassium dihydrogenphosphate), LiNbO3 (lithium niobate), Se, Te, LBO, BBO and KB5. LBO is especially preferable to be used. In a typical example, a second harmonic (532 nm) of an Nd:YVO4 laser oscillator device (a fundamental wave of 1064 nm) is used. A laser oscillation mode is in a single mode, which is a TEM00 mode.
Silicon, which is selected as most suitable material, has an absorption coefficient between 103 and 104 cm−1 in a visible light range. Therefore, in order to crystallize a substrate having a high visible light transmittance such as glass and the first shape of semiconductor region 104 formed into 30 to 200 nm thickness by means of silicon, radiation with light in a visible light range of a wavelength between 400 and 700 nm can selectively heat the semiconductor region to perform crystallization without damaging the underlying blocking layer 102. Concretely, a penetration depth of a light beam having a wavelength of 532 nm is about 100 nm to 1000 nm for an amorphous silicon film and can completely reach the inside of the first shape of semiconductor region 104 formed into 30 to 200 nm thickness. That is, heating from the inside of the semiconductor film is possible to evenly heat almost all of the semiconductor region in a radiation range of a laser beam.
A direction of laser beam radiation may be from a surface side of the substrate 101 on which the first shape of semiconductor region 104 is formed, as shown in
An outline of the first shape of semiconductor region 104 shown in
On the other hand, a crystal extending from a concave portion formed between convex portions disorders orientation and retards growth of a good crystal due to mutual interference of crystals growing from the both ends. That is to say, simultaneous growth on the basis of a plurality of crystal cores and its mutual interference cause growth of a grain boundary or distortion-accumulated crystal.
Then, a second shape of semiconductor region 107 is formed by etching as shown in
Thus, the second shape of semiconductor region 107 can be considered to be in an outline formed into one body by a plurality of rectangular semiconductor regions provided in parallel and a pair of semiconductor regions continuously connected to the rectangular semiconductor regions. In the respective plural rectangular semiconductor regions, providing electrodes crossing them through an insulating film can form a channel forming region. The second shape of semiconductor region 107 can be considered to be in a configuration formed into one body by a plurality of rectangular semiconductor regions disposed in parallel continuously connected in series and a pair of semiconductor regions continuously connected to the both ends of the rectangular semiconductor regions. The respective plural rectangular semiconductor regions are provided with an interval twice or more the length in a channel width direction of the above semiconductor region. Further, the plural rectangular semiconductor regions are characterized in that they extend in a direction parallel to the channel length direction or that a crystal orientation is aligned in the channel forming region.
The crystal growth progresses from the both of a convex end (seed region) 202 and a concave portion therebetween. Core generation of a crystal from the convex end (seed region) 202 is confined due to its sharp shape, so that there would be an effect of reducing core generation density and of confining crystal orientation, which can grow a crystal having a specific orientation (a region from C1 to C4). On the other hand, a crystal extending from the concave portion formed between the convex portions simultaneously grows on the basis of a plurality of crystal cores and mutual interference thereof leads growth of a grain boundary or distortion-accumulated crystal (a region from BC1 to BC5).
A continuous wave laser beam for radiation is not limited to a single linear laser beam, and a plurality of partially overlapping continuous wave laser beams 204 can be used for radiation to carry out crystallization equally.
The first shape of semiconductor region 201 can be considered to be integrally formed by a plurality of semiconductor regions 201 a to 201 d having a sharp convex top-end and disposed in parallel. Assuming that a width of the first shape of semiconductor region 201 is Ws, a width of the semiconductor regions 201 a to 201 d having a sharp convex top-end is Wss, good crystallization regions (C1 to C4) are Wst and a range of a grain boundary or a distortion-accumulated crystal, which is grown from the concave portion, is Wbc, ˝ to ⅕, preferably ⅓ of Wss is intentionally eliminated by Wbc to form Wst. Wst is preferably 0.5 to 1.0 μm in view of crystal growth extended in a single direction.
As shown in
Crystallization with a continuous wave laser beam 903 starts from the seed region 902, while uncontrolled crystallization also occurs from a sidewall portion of the first shape of semiconductor region 901. The outline shown in
A laser beam linearly condensed by cylindrical lenses 308 and 309 in a cross section of a radiation surface is obliquely incident on a surface of a substrate 320 put on the table 311. A point of focus is then shifted due to aberration such as astigmatism and a linear condensing surface can be formed on or in the vicinity of the radiation surface. The cylindrical lenses 308 and 309 made of composite quartz offer high transmittance. A coating on a surface of the lenses is employed so as to achieve transmittance of 99% or more for a wavelength of the laser beam. The shape of a cross section of the radiation surface is, of course, not limited to linear, but may be in any shape such as rectangle, ellipse and super ellipse. A ratio of a short axis to a long axis of the shape is within a range between 1 to 10 and 1 to 100, in any event. A wavelength transforming element 310 is provided so that a high harmonic can be obtained for a fundamental wave.
As a laser oscillator device, is employed a rectangular beam solid laser oscillator device, especially preferably, a slab laser oscillator device, as described above. Alternatively, it is possible to employ a solid laser oscillator device using a crystal, which consists of a crystal such as YAG, YVO4, YLF and YalO3 doped with Nd, Tm or Ho, in combination with a slab structure amplifier. As slab materials, may be used a crystal such as Nd:YAG, Nd:GGG (gadolinium gallium garnet) and Nd:GSGG (gadolinium scandium gallium garnet). Besides the above, it is also possible to employ a gas laser oscillator device or a solid laser oscillator device capable of continuous light emission. As a continuous wave solid laser oscillator device, is employed a laser oscillator device using a crystal, which consists of a crystal such as YAG, YVO4, YLF and YAlO3 doped with Cr, Nd, Er, Ho, Ce, Co, Ti or Tm. A fundamental wave of an oscillation wavelength oscillates at a wavelength of 1 μm to 2 μm, although it depends on materials to be doped. It is possible to employ a diode-exciting type of solid laser oscillator device to be cascade-connected in order to obtain higher output.
Further, moving the table 311 by means of the driving means 312 and 313 in two axial directions enables laser process of the substrate 320. Moving in one direction can be continuously performed at an equal speed of 1 to 200 cm/sec, preferably 5 to 50 cm/sec for a distance longer than a side length of the substrate 320, while in the other direction step-moving can be discontinuously performed for a distance almost equal to a longitudinal length of a elliptic beam. It is arranged that oscillation of a laser oscillator device 101 and the table 311 be synchronously operated by means of the information processing means 315 provided with microprocessors.
When a laser beam for radiation of the substrate 320 by a laser radiation device having such structure is moved relatively in the X or Y direction shown in the drawing, a desired region or all surface of a semiconductor film can be processed. As described above with reference to
Concrete examples of a method of manufacturing a semiconductor device according to the invention will be now described in details with reference to the drawings, using embodiments.
In this embodiment, an amorphous silicon film formed on an insulating surface is etched into a predetermined pattern in a photoetching method to form a first shape of semiconductor region, which is then crystallized by means of a continuous wave laser beam.
A region provided with a plurality of sharp convex top-end portions (seed region) 404 is formed at one end of the first shape of semiconductor region 403. Radiation with a laser beam from the region 404 allows a crystal to continuously grow with a crystal core appearing at the region 404 being a starting point.
Crystallization thus progresses from the region radiated with the laser beam 406 and continuous moving of a solid-liquid interface can provide a crystalline semiconductor 407.
The first shape of crystallized semiconductor region 403 is then photoetched to form the second shape of semiconductor regions 405 a and 405 b, as shown in
In such a crystallization method, radiation with a continuous wave laser beam enables growth of a crystal in which grains extend in a single direction. This can be practically achieved by setting a scanning speed at 5 to 100 cm/sec, although it is, of course, required to set at any time detailed parameters such as a scanning speed and energy density of a laser beam. A speed of crystal growth experienced a melt-solidification process by means of a pulse laser is said to be 1 m/sec. Scanning with a laser beam at the slower speed and gradually cooling the surface, however, allows a crystal to continuously grow in a solid-liquid interface, so that a grain size of a crystal can be practically enlarged.
The scanning of the laser beam in the embodiment 1 may be scanned not only in one direction but also back-and-forth strokes. In this case, the seed regions 404 a and 404 b may be provided at both sides of the first semiconductor region 403 as shown in the embodiment of
The embodiment 3 intends that an amorphous silicon film formed on an insulating surface is crystallized in advance and enlargement of a crystal grain by a continuous wave laser beam.
As shown in
Then, as shown in
Finishing heat treatment, the masking insulation film 504 is removed by etching so that the crystal silicon film 507 can be obtained as shown in
The crystal silicon film 507 is etched into a fixed pattern by photoetching as shown in
The crystal silicon film is melted by such an irradiation of the laser beam to be recrystallized. With this recrystallization, crystal growth that crystal grains extend in the scanning direction of the laser beam occurs. In this case, the crystal silicon film having uniform crystal faces is formed in advance so that precipitation of a crystal having a different crystal face and creation of dislocation can be prevented. In embodiments described below, the TFT can be formed by the same treatments as the embodiment 1.
In the same way as the embodiment 3, the glass substrate 501, the blocking layer 502 and the amorphous silicon film 503 are formed, and then Ni as the catalytic element is added over the surface. The method for adding Ni is not limited so that different method such as spin coating, vapor deposition and sputtering can be adopted. In case of the spin coating method, water solution containing 5 ppm nickel acetate is applied to form a layer including catalytic element 506 (
Then the amorphous silicon film 503 is crystallized by the 4 hours heat treatment at a temperature of 580° C. Consequently, the crystal silicon film 507 is obtained as shown in
As shown in
After the above, a continuous wave laser beam is used for radiation to form a crystalline silicon film 523. It is characterized that crystallization is improved in orientation due to an operation of a catalyst element and that an applicable range is widened under a radiating condition of a continuous wave laser beam to be used for radiation. The latter is also due to an operation of a catalyst element and caused by lowering of core forming temperature or crystallization starting temperature. As for the subsequent processes, it is possible to process as well as Embodiment 3.
As shown in
After the above, furnace annealing is carried out for a heating process at 450 to 600 degrees centigrade for 1 to 30 minutes. Alternatively, rapid thermal annealing (RTA) is carried out for a heating process at 500 to 750 degrees centigrade for 10 to 120 seconds, and then, a core of a crystal is formed in the first shape of semiconductor region 520 consisting of an amorphous semiconductor film. A first shape of crystalline semiconductor film 524 provided in its inside with a crystal core originated from a catalyst element is accordingly formed, as shown in
Crystallization is then performed by radiation with a continuous wave laser beam as shown in
A process of eliminating by gettering a catalyst element remaining in a crystalline silicon film 507 with concentration of 1019/cm3 or more may be added after forming the crystalline silicon film 507 in Embodiment 3 or 4.
As shown in
After the above, furnace annealing is carried out for a heating process at 600 degrees centigrade for 12 hours, or a heating process is carried out at 650 to 750 degrees centigrade for 30 to 60 minutes by lamp annealing or gas thermal annealing so as to segregate Ni added as a catalyst element on a gettering site 512. This process allows the concentration of a catalyst element of the crystalline silicon film 507 to be less than 1017/cm3.
The process can be advanced as well as Embodiment 3 or 4 after completing the gettering process. In gettering, the same process may be carried out after forming the first shape of semiconductor region. Further, it is also effective to perform the same process after forming the second shape of semiconductor region. Moreover, the same process may be carried out after the crystallization process by means of radiation with a continuous wave laser beam. In any case, gettering with enhanced crystallinity makes it easy to segregate a catalyst element such as Ni on a gettering site.
A TFT shown in
As shown in
In the embodiment 9, an example producing a CMOS type of TFT by using the second semiconductor region on an insulating film that is formed in the embodiments 1 to 8 will be described referring to
Crystalline structure is destroyed to become amorphous structure in a region where impurity elements are injected by the ion doping. In order to recover the crystalline structure and realize lower electrical resistance by activating the impurity elements, laser treatment is performed. The laser treatment can be done by the laser treatment machine as shown in
An interlayer insulating film 710 is formed by a silicon nitride film or a silicon oxide film as shown in
As described above, an n-channel type of TFT and a p-channel type of TFT are obtained. Though each TFT is shown as a single element in
A glass substrate or an organic resin substrate is used for a substrate 1101. Organic resin material is lighter in weight than glass material and effective in lightening a light emitting device per se. In manufacturing a light emitting device, organic resin material such as polyimide, polyethylene terephthalate (PET), polyethylene naphthalate (PEN), polyether sulphone (PES) and aramid is applicable. It is preferable to use barium borosilicate glass or alminoborosilicate glass, which is called non-alkali glass, for a glass substrate. A thickness of a glass substrate to be used is 0.5 to 1.1 mm, but it should be thinner for the purpose of lightening. It is desirable to use a glass substrate having small specific gravity of 2.37 g/cc in order to achieve further lightening.
These TFTs comprise a second shape of semiconductor regions 1103 to 1107, a gate insulating film 1108 and gate electrodes 1110 to 1113 on a blocking layer 1102 made of silicon nitride or silicon oxide nitride. A first insulating layer 1114 made of silicon nitride or silicon oxide nitride including hydrogen is formed on the gate electrode to function together with the blocking layer 1102 as a protection film for preventing impurities such as moisture or metal from spreading over and contaminating the second shape of semiconductor region.
A second insulating layer 1115, which is selected from organic resin material such as polyimide, polyamide, polyimide-amide, acrylic and BCB, is formed on the first insulating layer 1114 into a thickness of 0.5 to 1 μm as a flatting film. The second insulating layer 1115 is formed in firing after the organic compounds are applied by means of spin application method. Organic insulating body material is absorbent and has a characteristic of storing moisture. When the stored moisture is emitted again, it supplies the organic compounds of a light emitting element formed on the top layer portion with oxygen to cause deterioration of the light emitting element. A third insulating layer 1116 is formed on the second insulating layer 1115 into a thickness of 50 to 200 nm for the purpose of preventing moisture from being stored and emitted again. The third insulating layer 1116 should be a fine film in view of adhesiveness with a ground and a barrier characteristic. It is preferably formed by means of inorganic insulating material selected from silicon nitride, silicon oxide nitride, aluminum oxide nitride and aluminum nitride in sputtering method.
In the case of silicon nitride produced in sputtering method in which nitrogen is only used as a sputtering gas while silicon is used as a target, it is enough to have a film thickness of 10 to 100 nm, preferably, 20 to 40 nm. This sputtering method can be considered to have a reactive mechanism close to so-called reactive sputtering in which parent material of a target is not only scattered by means of diluted gas ion, but a surface of the target is nitrided to be adhered to a substrate. It is thus characterized that the mechanism allows a silicon nitride film finer than the case that silicon nitride is used as a target to be formed even at a room temperature. Similarly, a thickness should be 40 nm or more in the case of aluminum oxide nitride film produced in the sputtering method.
After the above, a contact hole is formed to form wirings 1117 to 1125. A fourth insulating layer 1128 is then formed of organic resin material especially in a pixel region in order to eliminate inequality of a surface due to the contact hole and the wirings. A fifth insulating layer 1129 consisting of a silicon nitride film is formed in the sputtering method on the organic resin material 1128 since the material 1128 is absorbent. The fourth insulating layer 1128 is not only formed in the pixel portion 1302 but extends to the driving circuit portion 1301. It also has a function as a layer insulating film when it is formed over the wirings 1117 to 1125.
A light emitting element 1309 is formed on the fifth insulating layer 1129. In a displaying device having a structure that a light is emitted through a substrate 1101, an ITO (indium tin oxide) layer is formed on the fifth insulating layer 1129 as an anode layer 1126. Zinc oxide or gallium may be added to ITO for the purpose of flattening and resistance lowering. The wiring 1123 is electrically connected to the anode layer 1126 through a contact hole in the pixel portion.
A protection insulating film 1130 is provided for preventing a light emitting element from short-circuiting due to inequality caused by an end of the anode layer 1126 formed in every pixel portion and a contact hole. The protection insulating film 1130 can consist of a silicon oxide film, a silicon nitride film or a silicon oxide nitride film. In the protection insulating film 1130, the organic insulating body material is first formed into a thickness of 0.5 to 2 μm over the whole surface, and then, an aperture is formed in accordance with the anode layer 1126.
The light emitting element 1309 consists of the anode layer 1126, a cathode layer 1132 including alkaline metal or alkaline earth metal and an organic compounds layer 1131 including a light emitting layer therebetween. The organic compounds layer 1131 including a light emitting layer comprises one or plurality layers piled. Each layer is distinctively called a hole injection layer, a hole carrying layer, a light emitting layer, an electron carrying layer and an electron injection layer in accordance with respective purposes and functions. These layers can be formed by means of any one of or all of small molecule organic compounds material, middle molecule organic compounds material and polymer-based organic compounds material appropriately in combination. Further, it is possible to form a mixed layer in which an electron carrying material and hole carrying material are mixed appropriately or mixed junction in which a mixed region is formed on each junction surface. It is, of course, also possible to provide a pixel structure in which an anode and a cathode are reversed.
The cathode layer 1132 consists of alkaline metal or alkaline earth metal having a small work function. Material including magnesium (Mg), lithium (Li) or calcium (Ca) is used for the cathode layer 1132. It is preferable to use an electrode made of MgAg (material formed by mixing Mg and Ag at a ratio of Mg:Ag=10:1). Further, an MgAgAl electrode, an LiAl electrode and an LiFAl electrode can also be used as other than the above. Moreover, the cathode layer 1132 can be formed by combining fluoride such as alkaline metal or alkaline earth metal and low resistance metal such as aluminum. The cathode layer 1132 is formed across plural pixels as a common electrode and is connected to a wiring 1120 outside the pixel portion 1302 or between the pixel portion 1302 and the driving circuit portion 1301 to be led to an outer terminal.
In order to improve airtightness, a sixth insulating layer 1133 may be formed on the above cathode layer 1132 by means of material selected from silicon nitride, diamond like carbon (DLC), aluminum oxide nitride, aluminum oxide and aluminum nitride. Especially, a DLC layer is known for its high characteristic in gas barrier for oxygen, CO, Co2, H2O and so on. A fifth inorganic insulating layer is desirably formed continuously after a cathode 131 is formed, without exposed to the air. A buffer layer made of silicon nitride may be provided under the fifth inorganic insulating layer to improve adhesiveness. It is also possible to form, on an interface between the anode layer 1126 and the organic compounds layer 1131 including a light emitting layer, an inorganic insulating layer having a thickness of 0.5 to 5 nm so that a tunnel current can flow, although the inorganic insulating layer is not shown in the drawings. The inorganic insulating layer is effective in prevention of short circuit caused by inequality of a surface of the anode and in restraining dispersion of alkaline metal used for a cathode to a lower layer side.
The structure shown in the drawing is, of course, only an example and does not form a requirement for constructing the invention.
A circuit structure of a driving circuit portion 1301 is omitted here although a gate signal side driving circuit is different from a data signal side driving circuit. An n-channel type of TFT 1303 and a p-channel type of TFT 1304 are connected to wirings 1118 and 1119. Using these TFTs, a shift resistor, a latch circuit and/or a buffer circuit can be formed.
An input terminal portion 1308 is formed by means of a wiring formed in the same layer with a gate electrode or a wiring formed on a third insulating layer 1116.
An adhesive resin 1134 is filled in the aperture and in the vicinity thereof to fix a sealing substrate 1135. Metals such as stainless steel and aluminum can be used for the sealing substrate 1135. A glass substrate may be also used. An inner part enclosed by the adhesive resin 1134 and the sealing substrate 1135 can be filled with a drier such as barium oxide to be sealed in order to prevent deterioration due to moisture. The sealing substrate may be formed by organic resin material having a thickness of around 0 to 120 μm so as to be flexible. A cover film consisting of inorganic insulating body such as DLC and silicon nitride may be formed on a surface of the sealing substrate as a gas barrier layer. An example of material used for a sealing pattern is epoxy adhesive. Further covering side portions with a cover film consisting of inorganic insulating body can prevent steam from penetrating from the side portions.
For an adhesive resin 1134, can be used a UV-curing type of acrylic resin or a cation UV-curing type of epoxy resin.
Accordingly, a TFT is combined with a light emitting element to form a pixel portion, and then, a displaying device can be completed. In such a displaying device, a driving circuit can be formed on the same substrate, using a TFT. As shown in
The invention can be applied for various electronic devices. The semiconductor devices include a mobile information terminal (an electronic note, a mobile computer, a cellular phone and so on), a video camera, a digital camera, a personal computer, a television set and a projection type of display apparatus. Examples are shown in
Electronic apparatus illustrated in this specification is an example, therefore the invention is applicable particularly, but not exclusively, to those examples.
As described above, in accordance with the invention, crystallization using a first shape of semiconductor region in which a plurality of semiconductor regions having on its one side a sharp convex top-end portion is disposed in parallel is performed by irradiation with a continuous wave laser beam, so that a crystal first formed in a seed region, which becomes a core, would grow. Growth of the core of the crystal is then confined to have an effect of reducing core generating density as well as confining orientation of a crystal, so that a crystal having a specific orientation can be grown. Arranging a region to consist of a crystal extending from a plurality of sharp convex top-end portions so as to eliminate a grain boundary extended from a concave portion or a distortion-accumulated crystal allows a TFT to be formed only with a good crystal.
In accordance with such a structure, a plurality of rectangular semiconductor regions are provided in parallel between a pair of source and drain regions to form a transistor, so that dispersion of a characteristic between elements can be made small. Further, only using good crystals can improve mobility of field effect.
|Cited Patent||Filing date||Publication date||Applicant||Title|
|US4330363||Aug 28, 1980||May 18, 1982||Xerox Corporation||Thermal gradient control for enhanced laser induced crystallization of predefined semiconductor areas|
|US4388145||Oct 29, 1981||Jun 14, 1983||Xerox Corporation||Laser annealing for growth of single crystal semiconductor areas|
|US4554823||Jun 25, 1984||Nov 26, 1985||The United States Of America As Represented By The Secretary Of The Army||Method for burning rate characterization of solid propellants|
|US4780590||Nov 21, 1985||Oct 25, 1988||Penn Research Corporation||Laser furnace and method for zone refining of semiconductor wafers|
|US5208476 *||May 31, 1991||May 4, 1993||Seiko Epson Corporation||Low leakage current offset-gate thin film transistor structure|
|US5214001||Jan 14, 1991||May 25, 1993||Mitsubishi Denki Kabushiki Kaisha||Method of manufacturing semiconductor device having planar single crystal semiconductor surface|
|US5225886||Sep 18, 1990||Jul 6, 1993||Hitachi, Ltd.||Method of and apparatus for detecting foreign substances|
|US5338959 *||Mar 30, 1993||Aug 16, 1994||Samsung Electronics Co., Ltd.||Thin film transistor with three dimensional multichannel structure|
|US5583362 *||Sep 14, 1994||Dec 10, 1996||Mitsubishi Denki Kabushiki Kaisha||Gate all around thin film transistor|
|US5632915||Aug 29, 1994||May 27, 1997||Gerber Garment Technology, Inc.||Laser material processing apparatus and a work table therefor|
|US5643826||Oct 25, 1994||Jul 1, 1997||Semiconductor Energy Laboratory Co., Ltd.||Method for manufacturing a semiconductor device|
|US5708252||Jan 22, 1996||Jan 13, 1998||Semiconductor Energy Laboratory Co., Ltd.||Excimer laser scanning system|
|US5712191||Sep 8, 1995||Jan 27, 1998||Semiconductor Energy Laboratory Co., Ltd.||Method for producing semiconductor device|
|US5731613||Aug 9, 1995||Mar 24, 1998||Semiconductor Energy Laboratory Co., Ltd.||Semiconductor device having a monocrystalline layer composed of carbon, oxygen, hydrogen and nitrogen atoms|
|US5808321||Jun 7, 1994||Sep 15, 1998||Semiconductor Energy Laboratory Co., Ltd.||Semiconductor device with recrystallized active area|
|US5854803||Dec 27, 1995||Dec 29, 1998||Semiconductor Energy Laboratory Co., Ltd.||Laser illumination system|
|US5937282||Jul 11, 1997||Aug 10, 1999||Semiconductor Energy Laboratory Co., Ltd.||Method for producing semiconductor device|
|US5959313||Sep 26, 1997||Sep 28, 1999||Semiconductor Energy Laboratory Co., Ltd.||Thin film semiconductor having a monocrystalline region containing carbon, nitrogen and oxygen and crystallization promotor metal component|
|US5986306||Dec 4, 1998||Nov 16, 1999||Semiconductor Energy Laboratory Co., Ltd.||Thin film transistor having a heat sink that exhibits a high degree of heat dissipation effect|
|US6060726 *||Apr 22, 1999||May 9, 2000||Lg Semicon Co., Ltd.||CMOS transistor with two channel regions and common gate|
|US6071765||Aug 20, 1997||Jun 6, 2000||Sony Corporation||Method of forming polycrystalline silicon layer on substrate and surface treatment apparatus thereof|
|US6210996||Dec 2, 1998||Apr 3, 2001||Semiconductor Energy Laboratory Co., Ltd.||Laser illumination system|
|US6242289||Apr 15, 1999||Jun 5, 2001||Semiconductor Energy Laboratories Co., Ltd.||Method for producing semiconductor device|
|US6365933||Oct 14, 1997||Apr 2, 2002||Semiconductor Energy Laboratory Co., Ltd.||Semiconductor device and method of manufacturing the same|
|US6413802 *||Oct 23, 2000||Jul 2, 2002||The Regents Of The University Of California||Finfet transistor structures having a double gate channel extending vertically from a substrate and methods of manufacture|
|US6449123||Jul 21, 2000||Sep 10, 2002||Sumitomo Special Metals Co., Ltd.||Methods for marking a sintered product and for fabricating magnetic head substrate|
|US6469729||Jun 30, 2000||Oct 22, 2002||Videojet Technologies Inc.||Laser marking device and method for marking arcuate surfaces|
|US6479329||May 14, 2001||Nov 12, 2002||Semiconductor Energy Laboratory Co., Ltd.||Method for producing semiconductor device|
|US6599788||Aug 17, 2000||Jul 29, 2003||Semiconductor Energy Laboratory Co., Ltd.||Semiconductor device and method of fabricating the same|
|US6677222||Aug 11, 2000||Jan 13, 2004||Fujitsu Limited||Method of manufacturing semiconductor device with polysilicon film|
|US6693257||Nov 28, 2000||Feb 17, 2004||Semiconductor Energy Laboratory Co., Ltd.||Laser irradiation apparatus, laser irradiation method, and method for manufacturing a semiconductor device|
|US6700096||Oct 25, 2002||Mar 2, 2004||Semiconductor Energy Laboratory Co., Ltd.||Laser apparatus, laser irradiation method, manufacturing method for semiconductor device, semiconductor device, production system for semiconductor device using the laser apparatus, and electronic equipment|
|US6730550||Aug 10, 2000||May 4, 2004||Semiconductor Energy Laboratory Co., Ltd.||Laser apparatus, laser annealing method, and manufacturing method of a semiconductor device|
|US6753212||Aug 21, 2001||Jun 22, 2004||Semiconductor Energy Laboratory Co., Ltd.||Laser apparatus, laser annealing method, and manufacturing method of a semiconductor device|
|US20010019861||Mar 20, 2001||Sep 6, 2001||Shunpei Yamazaki||Laser illumination system|
|US20010038127||Feb 28, 2001||Nov 8, 2001||Shunpei Yamazaki||Semiconductor device and a method of manufacturing the same|
|US20030047732||Jul 31, 2002||Mar 13, 2003||Semiconductor Energy Laboratory Co., Ltd.||Semiconductor device and manufacturing method thereof|
|US20030059990||Aug 21, 2002||Mar 27, 2003||Shunpei Yamazaki||Method for manufacturing semiconductor device|
|US20030075733||Sep 10, 2002||Apr 24, 2003||Semiconductor Energy Laboratory Co., Ltd.||Light emitting device and method of manufacturing a semiconductor device|
|US20030148594||Nov 7, 2002||Aug 7, 2003||Semiconductor Energy Laboratory Co., Ltd.||Laser apparatus, laser irradiating method, manufacturing method of semiconductor device, semiconductor device, manufacturing system of semiconductor device using the laser apparatus, and electronic device|
|US20030153182||Nov 27, 2002||Aug 14, 2003||Semiconductor Energy Laboratory Co., Ltd.||Laser irradiation apparatus|
|US20030153999||Nov 27, 2002||Aug 14, 2003||Semiconductor Energy Laboratory Co., Ltd.||Program for controlling laser apparatus and recording medium for recording program for controlling laser apparatus and capable of being read out by computer|
|US20030171837||Nov 21, 2002||Sep 11, 2003||Semiconductor Energy Laboratory Co., Ltd.||Semiconductor fabricating apparatus|
|US20030211714||Dec 13, 2002||Nov 13, 2003||Semiconductor Energy Laboratory Co., Ltd.||Irradiation method of laser beam|
|US20030215973||Dec 10, 2002||Nov 20, 2003||Semiconductor Energy||Manufacturing method of semiconductor device|
|US20030228723||Dec 9, 2002||Dec 11, 2003||Semiconductor Energy Laboratory Co., Ltd.||Laser irradiation method and method of manufacturing a semiconductor device|
|US20030235971||Nov 29, 2002||Dec 25, 2003||Semiconductor Energy Laboratory Co., Ltd.||Manufacturing method for a semiconductor device|
|US20040106237||Aug 16, 2002||Jun 3, 2004||Shunpei Yamazaki||Method for fabricating semiconductor device|
|US20040132266||Dec 19, 2003||Jul 8, 2004||Semiconductor Energy Laboratory Co., Ltd.||Laser apparatus, laser irradiation method, manufacturing method for semiconductor device, semiconductor device, production system for semiconductor device using the laser apparatus, and electronic equipment|
|US20040208206||Jan 14, 2004||Oct 21, 2004||Semiconductor Energy Laboratory Co., Ltd.||Laser irradiation apparatus, laser irradiation method, and method for manufacturing a semiconductor device|
|US20050041005||Aug 26, 2004||Feb 24, 2005||Semiconductor Energy Laboratory Co. Ltd.||Semiconductor device and fabrication method thereof|
|US20060175612||Apr 4, 2006||Aug 10, 2006||Semiconductor Energy Laboratory Co., Ltd.||Semiconductor device and fabrication method thereof|
|US20070085080||Dec 11, 2006||Apr 19, 2007||Semiconductor Energy Laboratory Co., Ltd.||Semiconductor device and method of manufacturing the same|
|EP0088004A2||Feb 16, 1983||Sep 7, 1983||The Bendix Corporation||Method for producing oriented islands of single crystal films|
|EP1049144A1||Dec 17, 1998||Nov 2, 2000||Matsushita Electronics Corporation||Semiconductor thin film, method of producing the same, apparatus for producing the same, semiconductor device and method of producing the same|
|JP2000068520A||Title not available|
|JP2001144027A||Title not available|
|JP2001156018A||Title not available|
|JP2001291666A||Title not available|
|JPH0864834A||Title not available|
|JPH0878329A||Title not available|
|JPH0974205A||Title not available|
|JPH02181419A||Title not available|
|JPH05226790A||Title not available|
|JPH07130652A||Title not available|
|JPH08195357A||Title not available|
|JPH09270393A||Title not available|
|JPH10135468A||Title not available|
|JPH10135469A||Title not available|
|JPH10289876A||Title not available|
|JPH11354463A||Title not available|
|JPS58156591A||Title not available|
|JPS59102890A||Title not available|
|JPS59184517A||Title not available|
|JPS60161396A||Title not available|
|JPS62104117A||Title not available|
|1||A. Hara et al. , "Ultra-high Performance Poly-Si TFTs on a Glass by a Stable Scanning CW Laser Lateral Crystallization", AMLCD'01 Tech. Dig., 2001, pp. 227-230.|
|2||Amendment and Response to Election Requirement filed in U.S. Appl. No. 11/636,598, filed on Dec. 22, 2008.|
|3||Hara, Akito et al., "High Performance Poly-Si TFT's on a Glass by a Stable Scanning CW Laser Lateral Crystallization", IEDM '01 Technical Digest of International Electron Devices Meeting, Jan. 1, 2001, pp. 747-750.|
|4||Office Action dated Apr. 2, 2009 in U.S. Appl. No. 11/636,598.|
|Citing Patent||Filing date||Publication date||Applicant||Title|
|US8860021||Dec 17, 2012||Oct 14, 2014||Semiconductor Energy Laboratory Co., Ltd.||Semiconductor element, method for manufacturing the semiconductor element, and semiconductor device including the semiconductor element|
|US9236428||Oct 8, 2014||Jan 12, 2016||Semiconductor Energy Laboratory Co., Ltd.||Semiconductor element, method for manufacturing the semiconductor element, and semiconductor device including the semiconductor element|
|U.S. Classification||257/66, 257/E29.292, 257/75, 257/E29.151, 257/49, 257/E29.003, 257/72, 257/E29.273, 257/74, 257/64, 257/E21.411|
|International Classification||H01L21/20, H01L21/77, H01L27/12, H01L29/786, H01L29/04, H01L21/336, H01L29/10, H01L21/84, G02F1/1368|
|Cooperative Classification||H01L29/04, H01L27/1214, H01L29/66757, H01L29/78675, H01L27/1285|
|European Classification||H01L29/786E4C2, H01L29/04, H01L29/66M6T6F15A2, H01L27/12T, H01L27/12T30B2C|