|Publication number||US4729892 A|
|Application number||US 06/842,337|
|Publication date||Mar 8, 1988|
|Filing date||Mar 21, 1986|
|Priority date||Mar 21, 1986|
|Also published as||CA1279819C|
|Publication number||06842337, 842337, US 4729892 A, US 4729892A, US-A-4729892, US4729892 A, US4729892A|
|Inventors||Paula T. Beall|
|Original Assignee||Ciba-Geigy Corporation|
|Export Citation||BiBTeX, EndNote, RefMan|
|Patent Citations (21), Non-Patent Citations (4), Referenced by (51), Classifications (12), Legal Events (5)|
|External Links: USPTO, USPTO Assignment, Espacenet|
Proton nuclear magnetic resonance (NMR) tomography has become an important tool in biomedical research and medical diagnosis. The image contrast mechanisms of NMR are different from X-ray imaging, and provide substantial contrast between certain soft tissues that are nearly identical using radiological techniques. Further, conventional radiological imaging techniques involve the use of high energy electromagnetic radiation associated with potential cancer induction, whereas the low energy radio waves associated with NMR poses no such risk. However, while some soft tissues provide substantial contrast using NMR techniques, others, particularly those involving the gastrointestinal tract, yield a relatively low level of contrast in proton NMR imaging. This has prompted the development of suitable NMR contrast agents. While numerous substances, such as vegetable oils and paramagnetic metal salt solutions, such as ferric chloride solutions and solutions of gadolinium oxide, have been used to visualize the lumen of the stomach and intestines in NMR tomography, none have the coating and filling characteristics which have made barium sulfate so useful in radiological applications. Moreover, many paramagnetic metal ion containing solutions e.g. those of Cu2+, Cr3+, Fe3+ and Mn2+, are generally toxic at concentrations which sufficiently shorten the spin relaxation times, T1 and T2, of the solution environment to render such solutions useful NMR contrast agents. Runge et al., Radiology, Vol. 147, pp. 789-791 (1983).
Further, since conventionally available proton NMR tomography equipment is complex in terms of operator selectable paramaters, there is a need for storage stable materials especially in the form of a collection or array, which substantially mimics the range of proton density values, spin-lattice or longitudinal relaxation (T1) values, and spin-spin or traverse relaxation (T2) values, associated with various animal tissue, for tuning such selectable parameters. Appropriate tuning of the operator selectable parameters enables the operator to optimize the desired contrast characteristics associated with NMR tomographic images, including, for example, inversion recovering images, partial saturation images, density images, spin echo images, and the like. See in general, Wehrli et al., Magnetic Resonance Imaging, Vol. 2, pp. 3-16 (1984).
It has now been surprisingly discovered that synthetic substantially non-degradable cross-linked water-swellable hydrogel materials, having in the swollen state between about 5 to about 95% water and containing functional groups which interact with water, possess nuclear magnetic resonance spin density values, and T1 and T2 values sufficiently analogous to the spectrum of values associated with mammalian tissue, such that the aqueous swollen materials are highly useful in proton NMR tomographic imaging techniques, and overcome many of the disadvantages associated with known materials and techniques.
It has been further unexpectedly discovered that those hydrogels having T1 and T2 values substantially shorter than that of gastro-intestinal viscera are highly useful as proton NMR image contrast agents.
Thus, it is an object of the instant invention to provide a method of contrasting a proton NMR tomograph of the gastro-instestinal tract, or a portion thereof, by administering to a mammal, including man, an effective image contrasting amount of a physiologically tolerable, synthetic substantially non-degradable cross-linked hydrogel having, in the aqueous swollen state, spin-lattice or spin-spin relaxation values substantially shorter than the surrounding gastro-intestinal tissue environment.
It is a further object of the instant invention to provide an aqueous coating suspension or slurry of particulate swollen synthetic substantially non-degradable cross-linked hydrogel, said hydrogel having spin-lattice or spin-spin relaxation values substantially shorter than the respective spin-lattice or spin-spin average relaxation values of gastro-intestinal viscera, for use as proton NMR contrast agents.
It is yet a further object of the instant invention to provide a collection or array of storage stable swollen cross-linked hydrogel materials possessing a range of nuclear magnetic resonance spin density values, spin-lattice relaxation values and spin-spin relaxation values, embracing at least a portion of the spectrum of such values possessed by distinct anatomic mammalian tissue, and suitable for use in NMR imaging equipment for proton NMR image contrast determinations.
These and other objects of the invention are apparent from the following disclosure.
One embodiment of the instant invention relates to a method of contrasting a proton NMR tomograph of the gastro-intestinal tract of a mammal, by administering to the mammal an effective image contrasting amount of a physiologically tolerable cross-linked synthetic substantially non-degradable hydrogel in particulate form, said hydrogel having, in the aqueous swollen state, spin-lattice or spin-spin relaxation times substantially shorter than the surrounding gastro-intestinal tissue environment, and subjecting the mammal to said proton NMR tomography.
The hydrogel particulate may be administered to the gastro-intestinal tract orally or rectally.
Conveniently, the hydrogel is administered as an aqueous suspension or slurry of particulate swollen cross-linked hydrogel. The size of the hydrogel particles can vary over a wide range, depending upon the desired resolution of the image desired, and the like. In general, the hydrogel particulate can range, in average diameter between about 100 and about 100 mm, preferably between about 1 mm and about 10 mm, and most preferably between about 2 mm and about 10 mm. The particulate hydrogel material may be in the form of beads, powders or granulates. Because of the crosslinked nature of hydrogels, they are substantially insoluble, but water-swellable, in aqueous media. Thus, the hydrogels are not absorbed through the gastro-intestinal walls upon administration. Accordingly, the image contrasting cross-linked hydrogels are generally well tolerated and avoid the toxic aspects associated with many paramagnetic metal ion solutions, due to the substantially non-degradable, i.e. non-digestible, nature of the hydrogel material.
In order for the aqueous swollen particulate cross-linked hydrogel material to exert an effective contrasting effect in proton NMR tomography of the gastro-intestinal tract, the hydrogen material chosen should, in the fully swollen state, exhibit relaxation time constants, T1 and T2, substantially less than that of gastro-intestinal viscera. In general, suitable hydrogels exhibit, at a proton resonance frequency of about 10 megahertz (MHZ), a T1 relaxation time of between about 10 to about 200 milliseconds (msec), preferably between about 10 to about 150 msec, and most preferably between about 20 to about 120 msec, and a T2 relaxation time of between about 1 to about 60 msec, preferably between about 1 to about 50 msec, most preferably between about 2 and about 50 msec. At about 10 megahertz, the T1 value of gastro-intestinal viscera characteristically is between about 150-700, and the T2 value is between about 20-100, msec.
As the proton resonance frequency is decreased, the respective T1 and T2 values of suitable image contrasting hydrogel materials likewise decrease, as do the T1 and T2 average values of gastro-intestinal viscera.
Similarly, as the proton resonance frequency of the NMR is increased, T1 and T2 values of suitable image contrasting hydrogel materials likewise increase, as do the average T1 and T2 values for the gastro-intestinal tract. The instant image contrasting materials are generally suitable throughout the conventional range of chosen proton resonance frequencies characteristically used in NMR tomography, e.g. between about 2 to about 30 MHZ.
Eligible cross-linked hydrogel materials suitable for use as contrast agents in NMR tomography of the gstro-intestinal tract are easily determined by simple comparison of sample swollen cross-linked hydrogel T1 and T2 values with the corresponding average value of gastro-intestinal tissue at a chosen proton resonance frequency. Such tests can be conducted in vitro, using representative actual or phantom tissue samples, or in vivo, using live test animals.
Typical hydrogels found to be suitable as NMR gastro-intestinal contrast agents characteristically contain between about 5% to about 80% water, more preferably between about 10% to about 75% water. The hydrogel is advantageously swollen with a saline solution for in vitro comparative purposes in order to mimic the environment of the gastro-intestinal tract.
Moreover, suitable synthetic substantially non-degradable hydrogel materials contain as part of the cross-linked, three dimensional matrix, hydrophilic functional groups which interact with water. As is well known, these functional groups are to a large extent responsible for the hydrophilic aqueous swelling ability of the hydrogels. Representative hydrophilic groups include hydroxyl, keto, amino, amido, ether, carboxy, sulfoxy, sulfonyl, and the like.
In general, the T1 and T2 relaxation times for a given hydrogel material will be proportional to the aqueous swelling ability of the material. Since the aqueous swellability can be decreased by increasing the amount of crosslinking of the hydrogel, the T1 and T2 values of the fully swollen hydrogel can be decreased by increasing the amount of crosslinking agent incorporated into the hydrogel material. It is believed that the T1 and T2 values are decreased as cross-linking is increased because the average compartment size for the absorbed water is reduced, thereby increasing the interaction between the water molecules and the hydrophilic components of the hydrogel matrix. Further, increasing the number of hydrophilic groups present in the hydrogel likewise tends to decrease the T1 and T2 relaxation times as the degree of interaction of absorbed water is dependent upon the amount and nature of such hydrophilic groups.
Suitable synthetic substantially non-degradable hydrogel materials include the known classes of pharmaceutically acceptable crosslinked hydrogel materials employed in the fields of soft contact lenses and pharmaceutical medicament diffusion carriers, including without limitation, those crosslinked hydrogel materials described in Wichterle et al. U.S. Pat. Nos. 2,976,576 and 3,220,960; Mueller et al. 4,136,250, 4,192,827 and 4,224,427; Siederman 3,639,524, 3,721,657 and 3,767,731; Ewell 3,647,736; O'Driscoll et al. 3,700,761, 3,822,196, 3,816,571 and 3,841,985; Steckler 3,532,679; Stamberger 3,758,448 and 3,772,235; Neefe 3,803,093; Tanaka et al. 3,813,447; Blank 3,728,317, Isen 3,488,111; and Ohkada et al. 4,347,198, the disclosures of which incorporated by reference herein, in toto.
Such hydrogels are generally prepared by polymerizing a monomer or mixture of monomers, either in the presence of a cross-linking agent to crosslink the polymer, or in the absence of a cross-linking agent to form a pre-crosslinked intermediate which is subsequently crosslinked with a crosslinking agent. Also in the polymerization step there may be present, in addition to a monomer or mixture of monomers, a polymer or prepolymer substrate upon which the monomers may be grafted, by polymerization, for example. Where mixtures of monomers are employed, the resulting copolymer may be random, alternating, block or graft copolymers depending upon the polymerization techniques, sequence of monomer addition, reaction conditions, nature and reactivity of the monomers employed, and the like.
Generally the monomer employed is hydrophilic in nature. However, mixtures of hydrophilic and hydrophobic monomers, preferably containing less than 50 mole percent hydrophobic constituents, may be employed. Alternatively, a hydrophobic monomer may be polymerized and subsequently converted to a hydrophilic species, for example as is well known in the polymerization and subsequent hydrolysis of vinyl acetate to form polyvinyl alcohol, which may then be cross-linked with glyoxal, diglycidyl ether or the like.
Suitable hydrophilic monomers commonly employed in the preparation of crosslinked hydrogels useful in the instant invention include, without limitation, acrylic and/or methacrylic acid and the water-soluble derivatives thereof such as the epoxy or hydroxy substituted lower alkyl esters thereof including e.g. the 2-hydroxyethyl, glycidyl, 3-hydroxypropyl, or 2,3-dihydroxypropyl esters thereof; the ethoxylated and polyethoxylated hydroxy substituted lower alkyl esters thereof; the di-(lower alkyl) aminoloweralkyl acrylates or methacrylates, such as the 2-(dimethylamino)ethyl acrylate, or the 2-(diethylamino)ethyl methacrylate; the water soluble amides thereof, such as the unsubstituted amides and amides substituted by one or two hydroxyloweralkyl groups, such as N-(2-hydroxyethyl)-methacrylamide; water soluble heterocyclic nitrogen containing monomers, such as N-vinylpyrolidone, N-vinyl-succinimide, N-vinyl-pyrrole, 2- and 4-vinylpyridine, 4-vinyl-quinoline, 4-acrylylmorpholine and the like, mono-olefinic sulfonic acids and their pharmaceutically acceptable salts, such as sodium ethylene sulfonate, sodium styrene sulfonate and the like; hydroxyloweralkyl maleates, fumarates and vinyl ethers, such as 2-hydroxyethyl monomaleate, di(2-hydroxyethyl) maleate, 2-hydroxyethyl vinyl ether, 4-hydroxybutyl vinyl ether and the like.
Preferably, for patient administration the crosslinked hydrogels are substantially free of strongly ionic groups, such as sulfonates, free amine groups and the like, which may adversely interact with gastro-intestinal fluids and upset the electrolytic balance.
Suitable hydrophobic monomers which may be employed include, without limitation, C1-18 alkyl acrylates or methacrylates; vinyl acetate; C1-18 alkenes which are unsubstituted or substituted by halo; acrylonitrile; styrene; di-lower alkyl-acrylamides and -methacrylamides, vinyl Cl-5 alkyl ethers, such as propyl vinyl ether, and the like.
Suitable crosslinking agents include, without limitation, divinyl benzene, ethylene glycol dimethacrylate, polyethyleneglycol dimethacrylate, glyoxal, diglycidyl ether, and macromer cross-linking agents such as polytetramethylene oxide having a molecular weight of about 1500 which is capped at both ends by isophorone diisocyanate or 2,4-toluene diisocyanate and subsequently terminated by 2-hydroxyethylmethacrylate, e.g. as described in U.S. Pat. No. 4,277,582, or a polysiloxane having a molecular weight of about 400 to about 8500 capped at both ends with 2,4-toluene diisocyanate or isophorone diisocyanate and subsequently terminated by 2-hydroxymethacrylate, e.g. as described in U.S. Pat. No. 4,136,250.
If desired, the hydrogel materials may be formulated in the presence of a radio-opaque substance, such as particulate barium sulfate, iobenzamic acid, iocarmic acid, iocetamic acid, iodamide, iodipamide and pharmaceutically acceptable salts thereof. Alternately, the hydrogels may be prepared in the presence of tomographic inhancing aids such as ferric (Fe+3) and/or manganese (Mn+5) salts to increase the contrast of the hydrogel material in comparison with the surrounding tissues. A preferred method of preparing hydrogel beads by suspension polymerization is described in U.S. Pat. No. 4,224,427. In such process one may incorporate the aforementioned adjuvant ingredients, e.g. for rendering such beads radio-opaque or for enhancing NMR contrast, simply by adding the adjuvant to the suspension polymerization medium. The amount of adjuvant present will vary, dependent upon the nature thereof. Preferably, no more than 10 percent by weight of hydrogel consists of such adjuvant.
The hydrogel material generally is administered to the patient orally or rectally as an aqueous slurry or suspension. As the hydrogel material is soft, flexible and substantially inert, the slurry or suspension is generally very well tolerated by the patient.
Also, a collection or array of diverse hydrogel samples, possessing varying T1 and T2 constants, preferably exhibiting T1 and T2 constants embracing at least a substantial portion of the spectrum of such constants exhibited by diverse mamalian tissues may be employed as tissue phantom kits for adjusting tomography equipment. Generally, at least three such samples are employed in such kits.
The following examples are presented for the purpose of illustration only and are not to be construed to limit the nature or scope of the invention in any manner whatsoever. All parts are by weight unless otherwise specified.
In accordance with the procedure set forth in Example 1 of U.S. Pat. No. 4,224,427, 48 parts by weight of a macromer, 20 parts N-vinyl pyrrolidone and 32 parts of 2-hydroxyethyl methacrylate were polymerized using 0.2 parts of tert-butyl peroctoate as a free radical initiator. The macromer consists of poly(tetramethylene oxide) glycol having an average molecular weight of approximately 2000 endcapped with isophorone diisocyanate in an amount of two moles per mole of said glycol, and terminated with 1 mole of 2-hydroxyethyl methacrylate per mole of said diisocyanate, reacted for 72 hours at room temperature. The reaction mixture of macromer and monomers with initiator are combined in about 240 parts of an aqueous suspension of magnesium hydroxide (prepared by combining about 180 parts of a 20% by weight aqueous sodium chloride solution with about 12 parts of magnesium chloride hexahydrate with stirring at about 80° C. and adding dropwise about 60 parts of a 1-normal sodium hydroxide solution) with stirring at 150 rpm under a nitrogen blanket at 80° C., the macromermonomer mixture allowed to polymerize for 3 hours, and the temperature raised to 100° C. for one hour, after which the reaction medium is cooled to room temperature, the magnesium hydroxide suspending agent neutralized with concentrated hydrochloric acid and the reaction mixture beads isolated by filtration and washed with water to remove any residual monomer. The resulting polymer spherical beads (diameter approx. 1 mm) have a water content of approximately 56% by weight, based upon the weight of swollen crosslinked hydrogel polymer beads. Upon subjecting the swollen crosslinked polymer beads to NMR imaging at 6.4 MHz the following T values were obtained:
T1 =320±34 ms
T2 =52±3 ms.
Following the method of Example 1 a crosslinked hydrogel in the form of beads having a diameter of approx. 1 mm and containing 30% by weight of the macromer of Example 1 and 70% by weight 2-hydroxyethyl methacrylate are prepared. The resulting aqueous swollen beads contain approximately 25% by weight water and when subjected to NMR imaging at 6.4 MHz exhibit the following T values:
Following the method of Example 1, crosslinked hydrogel beads containing 12% by weight of the macromer of Example 1, 40% by weight n-octyl methacrylate, 27% by weight hydroxyethyl methacrylate are prepared. The resulting aqueous swollen beads contain approximately 27% by weight water and when subjected to NMR imaging at 6.4 MHz exhibit the following T values:
Following the method of Example 1, crosslinked hydrogel beads containing 30% of the macromer of Example 1, 20% 2-hydroxyethyl methacrylate and 50% methyl methacrylate are prepared. The resulting aqueous swollen beads contain approximately 9.9% water and when subjected to NMR imaging at 6.4 MHz exhibit the following T values:
Crosslinked hydrogel buttons having a diameter of about 20 mm and a height of about 10 mm are prepared by placing in a mold a mixture of 50 parts by weight 2-hydroxyethyl methacrylate, 50 parts by weight dimethyl acrylamide and 0.5 parts ethyleneglycol dimethacrylate in the presence of about 0.1 part benzoin methyl ether as initiator and polymerizing the reaction mixture under ambient conditions in the presence of an ultraviolet light source for about 8 hours. Upon swelling the crosslinked hydrogel with water, the equilibrated swollen material contained 79.8% water by weight, and when subjected to NMR imaging at 6.4 MHz exhibits the following T values:
T1 =1470±300 ms
T2 =174±30 ms.
Alternatively, the aforementioned monomer mixture is polymerized in a mold to form substantially spherical beads of crosslinked hydrogel having an average diameter of about 2 mm, which upon equilibration with water under ambient conditions contains approximately 80% water by weight.
Using the methods of Example 6, buttons and spherical beads, respectively, are prepared from a monomer mixture containing 75 parts 2-hydroxyethyl methacrylate, 25 parts dimethylacrylamide, 0.5 parts ethyleneglycol dimethacrylate as crosslinker and about 0.1 part benzoin methyl ether as polymerization initiator. The products, upon equilibration with water, contain approximately 59 weight percent water and having the following T values at 6.4 MHz:
T1 =250 ±60
T2 =56 ±10.
Using the methods of Example 6, buttons and spherical beads, respectively, are prepared from a mixture of 100 parts 2-hydroxyethyl methacrylate, 0.5 parts ethyleneglycol dimethacrylate and about 0.1 parts benzoin methyl ether. The products, upon equilibration with water, contain 39.3% water, a T1 value of 1850±300 and a T2 value of 224±100 (at 6.4 MHz).
Using the methods of Example 6, buttons and spherical beads, respectively, are prepared from a mixture of 75 parts 2-hydroxyethyl methacrylate, 25 parts methylmethacrylate, 0.5 parts ethyleneglycol dimethacrylate and 0.1 part benzoin methyl ether. The products upon equilibration with water, possess a water content of 22.7% by weight, a T1 value of about 1050 and a T2 value of 248±90 (at 6.4 MHz).
Using the methods of Example 6, buttons and sperical beads, respectively, are prepared from a mixture of 80 parts methylmethacrylate, 20 parts dimethylacrylamide, 0.5 parts ethyleneglycol dimethacrylate and about 0.1 part benzoin methyl ether. The products, upon equilibration with water, had a water content of 12.5% by weight and, at 6.4 MHz, a T1 value of 1440±700 and a T2 value of 234±100.
Using the methods of Example 6, buttons and spherical beads, respectively, are prepared from a mixture of 30 parts 2-hydroxyethyl methacrylate, 40 parts methyl methacrylate, 30 parts dimethylacrylamide, 0.5 parts ethyleneglycol dimethacrylate and about 0.1 part benzoin methyl ether. The products, upon equilibration with water, have a water content of 27.6% by weight and at 6.4 MHz exhibit a T1 of 220±110 and a T2 of 40±19.
Using the methods of Example 6, buttons and spherical beads, respectively, are prepared from a mixture of 70 parts methyl methacrylate, 30 parts dimethyl acrylamide, 0.5 parts ethyleneglycol dimethacrylate, and 0.1 part benzoin methyl ether. The products produced posess upon equilibration with water, a water content of 22.8% and, at 6.4 MHz, a T2 value of 38±50.
Upon the methods of Example 6, buttons and spherical beads, respectively, are prepared from a mixture of 50 parts of a fluorinated methacrylate ester of the formula
Rf --CH2 CH2 --SCONHCH2 CH2 OCO--C(CH3) =CH2
wherein Rf is a 1:1 mixture of n-C8 F17 and n-C10 F21, 30 parts methyl methacrylate and 20 parts dimethyl acrylamide, with 0.2 parts ethyleneglycol dimethacrylate and about 0.1 part benzoin methyl ether. The fluorinated methacrylate is prepared by combining one mole of perfluoroalkylthiol of the formula Rf CH2 CH2 SH per mole of 2-isocyanatoethyl methacrylate, adding to the reaction mixture 0.005 mole triethylamine per mole of thiol with mixing under ambient conditions to promote the reaction, reacting the resulting mixture at about 30° C. for 6 hours, and washing the resulting product with ethanol to remove unreacted material.
The crosslinked hydrogel, upon equilibration in water, had a water content of 11.6%, and, at 6.4 MHz, a T1 value of 730±300 and a T2 value of 172±105.
Using the methods of Example 6, buttons and spherical beads, respectively, are prepared from a mixture of 50 parts methyl methacrylate, 50 parts hydroxyethyl methacrylate, 0.5 parts ethylene glycol dimethacrylate, and about 0.1 part benzoin methyl ether. The resulting crosslinked hyrogel upon equilibration exhibits a water content of 13.9%, a T1 value of 300±200 and a T2 value of about 64 at 6.4 MHz.
A siloxane macromer is prepared according to Example 8 of U.S. Pat. No. 4,136,250. A mixture of 30 parts of the siloxane macromer, consisting of polydimethyl siloxane triol (Dow Corning 1248) having a molecular weight of about 6000 which is endcapped with isophorone diisocyanate in an amount of 3 moles per mole of siloxane and terminated with 2-hydroxyethyl methacrylate in an amount of 3 moles per mole siloxane, is combined with 40 parts methyl methacrylate and 30 parts dimethyl acrylamide, and 0.1 parts dimethyl acrylamide, and 0.1 part azobisiso-butyronitrile catalyst. The mixture is then cast as buttons having a dimater of about 20 mm and a height of about 10 mm, and as spherical beads having an average diameter of about 2 mm and cured at a temperature of 50° for 16 hours following by a post cure of 100° C. for one hour. Upon equilibration with water, the cross-linked polymer had a water content of 27.1%, and at 64 MHz a T1 value of 170±70 and T2 value of 42±7.
The procedure of Example 15 is repeated using 30 parts of the siloxane macromer with 20 parts of dimethyl/acrylamide and 50 parts methyl methacrylate. The resulting products upon equilibration contain 13.4% water and at 6.4 MHz have a T1 value of 290±50.
An array of aqueous swollen hydrogel buttons of Examples 6, 13, 14 and 15 are aligned in a whole body NMR imaging device at 6.4 MHz to obtain T1 values of 1470±300 ms, 730±300, 300±200 and 170±70. This compares favorably with tissue samples subjected to NMR imaging at 6.4 MH2, i.e. the T1 value of minced brain obtained is 1470±300; pancreas tissue is 730±300; heart muscle is 390±120; and liver is 170±70.
Using the procedure of Example 15, the macromer of Example 1 is reacted with various amounts of selected monomers to obtain crosslinked hydrogels which after equilibration in water are subjected to NMR imaging at 5 MHz to obtain the following results;
______________________________________Composition, %.sup.(1)Product MAC MMA DMA NVP HEMA EHA______________________________________18a 30 7018b 30 42 2818c 20 45 3518d 12 27.5 33 27.5______________________________________PropertiesProducts T1 T2 % H2 O______________________________________18a 155 16 23.018b 34 4 25.418c 43 4 49.018d 115 17 8.0______________________________________ .sup.(1) MAC = macromer of Example 1 MMA = methyl methacrylate DMA = dimethyl acrylamide NVP = N--vinyl pyrrolidone HEMA = 2hydroxyethyl methacrylate EHA = 2ethylhexyl acrylate
When subjected to NMR imaging at 30 MH2, the products of Examples 18a give a T1 value of 555±50; 18b gave a T1 value of 259±29, 18c gave a T1 value of 252±10 and 18d gave a T1 value of 252±8. The products of 18b and 18c are especially useful due to their high contrast, as image contrast agents. All of the products of 18a-18d are useful as image contrast agents in NMR imaging machines employing a combination of T1 and T2 in their imaging technique.
Also, the hydrogels of Examples 7, 11, 15 and 16 are highly valuable as image contrast agents due to their high contrast in the gastro-intestinal tract.
|Cited Patent||Filing date||Publication date||Applicant||Title|
|US2976576 *||Apr 24, 1956||Mar 28, 1961||Wichterle Otto||Process for producing shaped articles from three-dimensional hydrophilic high polymers|
|US3220960 *||Dec 21, 1960||Nov 30, 1965||Wichterle Otto||Cross-linked hydrophilic polymers and articles made therefrom|
|US3488111 *||Mar 16, 1967||Jan 6, 1970||Nat Patent Dev Corp||Hydrophilic hydrogel corneal contact lens with hard central insert|
|US3532679 *||Apr 7, 1969||Oct 6, 1970||Robert Steckler||Hydrogels from cross-linked polymers of n-vinyl lactams and alkyl acrylates|
|US3639524 *||Jul 28, 1969||Feb 1, 1972||Maurice Seiderman||Hydrophilic gel polymer insoluble in water from polyvinylpyrrolidone with n-vinyl-2-pyrrolidone and methacrylic modifier|
|US3647736 *||May 25, 1970||Mar 7, 1972||Kontur Kontact Lens Co Inc||Hydrophilic contact lens material|
|US3700761 *||Nov 28, 1969||Oct 24, 1972||Griffin Lab Inc||Fabrication of soft plastic contact lens blank|
|US3721657 *||Nov 23, 1970||Mar 20, 1973||M Seiderman||Hydrophilic gel polymers of vinylpyrrolidine and hydroxyalkyl methacrylate|
|US3728317 *||May 3, 1971||Apr 17, 1973||Hydrophilics Int Inc||Optical contact lenses and related devices|
|US3758448 *||Oct 5, 1971||Sep 11, 1973||Union Optics Corp||Copolymers and hydrogels of unsaturated esters|
|US3767731 *||Dec 20, 1971||Oct 23, 1973||M Seiderman||Contact lenses from hydrophilic gel polymers of polyvinylpyrrolidone monomeric vinylpyrrolidone and methacrylic modifier|
|US3772235 *||Oct 5, 1971||Nov 13, 1973||Union Optics Corp||Copolymers and hydrogels of unsaturated heterocyclic compounds|
|US3803093 *||Aug 18, 1972||Apr 9, 1974||C Neefe||Methyl methacrylate copolymer which may be hydrated|
|US3813447 *||Sep 15, 1971||May 28, 1974||Toyo Contact Lens Co Ltd||Hydrophilic synthetic high polymers for soft contact lenses and a process for manufacturing the same|
|US3816571 *||Aug 25, 1972||Jun 11, 1974||Warner Lambert Co||Fabrication of soft plastic lens|
|US3822196 *||Aug 25, 1972||Jul 2, 1974||Warner Lambert Co||Fabrication of soft plastic contact lens blank and composition therefor|
|US3841985 *||Aug 25, 1972||Oct 15, 1974||Warner Lambert Co||Irradiated composition for soft contact lens|
|US4136250 *||Jul 20, 1977||Jan 23, 1979||Ciba-Geigy Corporation||Polysiloxane hydrogels|
|US4192827 *||Mar 3, 1978||Mar 11, 1980||Ciba-Geigy Corporation||Water-insoluble hydrophilic copolymers|
|US4224427 *||Jun 1, 1978||Sep 23, 1980||Ciba-Geigy Corporation||Process for preparing hydrogels as spherical beads of large size|
|US4347198 *||Sep 25, 1980||Aug 31, 1982||Toray Industries, Ltd.||Producing soft contact lenses|
|1||*||Runge et al., Radiology, vol. 147, pp. 789 791 (1983).|
|2||Runge et al., Radiology, vol. 147, pp. 789-791 (1983).|
|3||*||Wehrli et al, Magnetic Resonance Imaging, vol. 2, pp. 3 16 (1984).|
|4||Wehrli et al, Magnetic Resonance Imaging, vol. 2, pp. 3-16 (1984).|
|Citing Patent||Filing date||Publication date||Applicant||Title|
|US4967764 *||Oct 24, 1988||Nov 6, 1990||The United States Of America As Represented By The Department Of Health And Human Services||Pressure sensor element to measure contact stress|
|US5023185 *||Dec 4, 1989||Jun 11, 1991||Nippon Oil Co., Ltd.||Method for determining resolution power or discrimination capacity of an NMR imaging apparatus|
|US5045304 *||Aug 31, 1988||Sep 3, 1991||Wayne State University||Contras agent having an imaging agent coupled to viable granulocytes for use in magnetic resonance imaging of abscess and a method of preparing and using same|
|US5071602 *||Aug 1, 1990||Dec 10, 1991||Nippon Oil Co., Ltd.||Method of making phantom for nmr diagnosis|
|US5079006 *||Jul 13, 1988||Jan 7, 1992||Aprex Corporation||Pharmaceutical compositions containing a magnetically detectable material|
|US5125408 *||Sep 19, 1991||Jun 30, 1992||The United States Of America As Represented By The Of The Department Of Health And Human Services||Pressure sensor element and method to measure contact stress|
|US5145661 *||Jul 15, 1991||Sep 8, 1992||Wayne State University||Method and contrast agent for use in magnetic resonance imaging of abscess|
|US5312755 *||Aug 14, 1991||May 17, 1994||Wisconsin Alumni Research Foundation||Contrast resolution tissue mimicking phantoms for nuclear magnetic resonance imaging with stable NMR properties|
|US5368840 *||Oct 13, 1992||Nov 29, 1994||Imarx Pharmaceutical Corp.||Natural polymers as contrast media for magnetic resonance imaging|
|US5370901 *||Jan 23, 1992||Dec 6, 1994||Bracco International B.V.||Compositions for increasing the image contrast in diagnostic investigations of the digestive tract of patients|
|US5380514 *||Mar 21, 1991||Jan 10, 1995||The Victoria University Of Manchester||Method for magnetic resonance imaging of internal body tissues using polysiloxanes|
|US5385719 *||Sep 22, 1992||Jan 31, 1995||Unger; Evan C.||Copolymers and their use as contrast agents in magnetic resonance imaging and in other applications|
|US5393525 *||Mar 21, 1994||Feb 28, 1995||Nycomed Imaging As||Contrast medium comprising superparamagnetic or ferromagnetic particles capable of increasing viscosity after administration|
|US5458127 *||Sep 13, 1994||Oct 17, 1995||Imarx Pharmaceutical Corp.||Copolymers and their use as contrast agents in magnetic resonance imaging and in other applications|
|US5517993 *||Jun 7, 1995||May 21, 1996||Imarx Pharmaceutical Corp.||Copolymers and their use as contrast agents in magnetic resonance imaging and in other applications|
|US5532006 *||Apr 23, 1993||Jul 2, 1996||The Board Of Trustees Of The University Of Illinois||Magnetic gels which change volume in response to voltage changes for MRI|
|US5551429 *||Jun 2, 1995||Sep 3, 1996||Fitzpatrick; J. Michael||Method for relating the data of an image space to physical space|
|US5624661 *||Jun 5, 1995||Apr 29, 1997||Unger; Evan C.||Hypoosmotic compositions comprising a polymer and a complexed contrast agent for MRI|
|US5645816 *||Jun 6, 1995||Jul 8, 1997||Imarx Pharmaceutical Corp.||Synthetic polyuronic and hypoosmotic polymer compositions in admixture with proteinaceously bound contrast agents for MRI|
|US5653959 *||Jun 8, 1994||Aug 5, 1997||Sintetica Sa||Compositions for increasing the image contrast in diagnostic investigations of the digestive tract of patients|
|US5658550 *||May 31, 1994||Aug 19, 1997||Imarx Pharmaceutical Corp.||Non cross-linked synthetic polymers as contrast media for magnetic resonance imaging|
|US5681542 *||Jun 7, 1995||Oct 28, 1997||Imarx Pharmaceutical Corp.||Compositions comprising a biocompatible gas and a polymer for magnetic resonance imaging|
|US5688490 *||Feb 7, 1996||Nov 18, 1997||Bracco International B.V.||Mucoadhesive compositions for increasing the ultrasonic image contrast of the digestive tract|
|US5730130 *||Jun 2, 1995||Mar 24, 1998||Johnson & Johnson Professional, Inc.||Localization cap for fiducial markers|
|US5792445 *||Feb 7, 1996||Aug 11, 1998||Bracco International B.V.||Polymers and copolymers of acrylic acid MRI of the digestive tract of patients|
|US5985244 *||Mar 26, 1997||Nov 16, 1999||Imarx Pharmaceutical Corp.||Polymers with a gas magnetic resonance imaging|
|US6318146 *||Jul 14, 1999||Nov 20, 2001||Wisconsin Alumni Research Foundation||Multi-imaging modality tissue mimicking materials for imaging phantoms|
|US6333971||Dec 22, 2000||Dec 25, 2001||George S. Allen||Fiducial marker|
|US6410616 *||Apr 7, 1999||Jun 25, 2002||Nippon Shokubai Co., Ltd||Crosslinked polymer particle and its production process and use|
|US6635486||Jul 27, 2001||Oct 21, 2003||Wisconsin Alumni Research Foundation||Multi-imaging modality tissue mimicking materials for imaging phantoms|
|US6675035||Jun 12, 1998||Jan 6, 2004||Imaging Diagnostic Systems, Inc.||Phantom for optical and magnetic resonance imaging quality control|
|US6965235||Jul 24, 2003||Nov 15, 2005||General Electric Company||Apparatus to simulate MR properties of human brain for MR applications evaluation|
|US7419376 *||Aug 14, 2006||Sep 2, 2008||Artahn Laboratories, Inc.||Human tissue phantoms and methods for manufacturing thereof|
|US7462488||May 27, 2005||Dec 9, 2008||Wisconsin Alumni Research Foundation||Tissue mimicking elastography phantoms|
|US7642775||Aug 19, 2005||Jan 5, 2010||Koninklijke Philips Electronics N.V.||MR method of determining local relaxation time values using calibrated phantom|
|US8163326 *||Dec 12, 2006||Apr 24, 2012||Boston Scientific Scimed, Inc.||Implantable or insertable medical devices visible under magnetic resonance imaging|
|US20030100830 *||Nov 27, 2001||May 29, 2003||Sheng-Ping Zhong||Implantable or insertable medical devices visible under magnetic resonance imaging|
|US20040067591 *||Oct 4, 2002||Apr 8, 2004||Wisconsin Alumni Research Foundation||Tissue mimicking elastography phantoms|
|US20050227364 *||May 27, 2005||Oct 13, 2005||Wisconsin Alumni Research Foundation||Tissue mimicking elastography phantoms|
|US20070167735 *||Dec 12, 2006||Jul 19, 2007||Sheng-Ping Zhong||Implantable or insertable medical devices visible under magnetic resonance imaging|
|US20080076099 *||Aug 14, 2006||Mar 27, 2008||Artann Laboratories, Inc.||Human tissue phantoms and methods for manufacturing thereof|
|US20080077006 *||Aug 19, 2005||Mar 27, 2008||Koninklijke Philips Electronics, N.V.||Mr Method of Determining Local Relaxation Time Values Using Calibrated Phantom|
|US20140356967 *||Dec 21, 2012||Dec 4, 2014||Hitachi, Ltd.||Tissue mimicking phantom and calibration device|
|EP0409351A1 *||Jul 19, 1990||Jan 23, 1991||Nycomed Imaging As||Contrast medium composition|
|EP0502814A2 *||Feb 5, 1992||Sep 9, 1992||BRACCO International B.V.||Compositions for increasing the image contrast in imaging of the digestive tract of patients|
|EP0693288A1 *||Apr 9, 1991||Jan 24, 1996||UNGER, Evan C||Polymers as contrast media for magnetic resonance|
|WO1991001148A1 *||Jul 19, 1990||Feb 7, 1991||Cockbain Julian R M||Contrast medium composition|
|WO1991015753A1 *||Apr 9, 1991||Oct 17, 1991||Evan C Unger||Polymers as contrast media for magnetic resonance imaging|
|WO1993010163A2 *||Nov 12, 1992||May 27, 1993||Nepera Inc||Adhesive hydrogels having extended use lives and process for the preparation of same|
|WO1994008509A1 *||Sep 23, 1993||Apr 28, 1994||Evan C Unger||Polymers as contrast media for magnetic resonance imaging|
|WO2008021720A2 *||Jul 31, 2007||Feb 21, 2008||Artann Lab Inc||Human tissue phantoms and methods for manufacturing thereof|
|U.S. Classification||424/9.3, 600/420, 436/173, 436/806|
|International Classification||A61K49/18, G01R33/28|
|Cooperative Classification||Y10T436/24, Y10S436/806, A61K49/1803, G01R33/5601|
|European Classification||G01R33/56B, A61K49/18F|
|Dec 11, 1987||AS||Assignment|
Owner name: CIBA-GEIGY CORPORATION, 444 SAW MILL RIVER ROAD, A
Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:BEALL, PAULA T.;REEL/FRAME:004797/0507
Effective date: 19860321
|Aug 19, 1991||FPAY||Fee payment|
Year of fee payment: 4
|Sep 5, 1995||FPAY||Fee payment|
Year of fee payment: 8
|Aug 31, 1999||FPAY||Fee payment|
Year of fee payment: 12
|Aug 22, 2000||AS||Assignment|