|Publication number||US3846353 A|
|Publication date||5 Nov 1974|
|Filing date||8 Jun 1970|
|Priority date||8 Jun 1970|
|Publication number||US 3846353 A, US 3846353A, US-A-3846353, US3846353 A, US3846353A|
|Original Assignee||Department Of Health Education|
|Export Citation||BiBTeX, EndNote, RefMan|
|Patent Citations (4), Non-Patent Citations (1), Referenced by (65), Classifications (10)|
|External Links: USPTO, USPTO Assignment, Espacenet|
United States Patent [191 Grotta Nov. 5, 1974 NONTHROMBOGENIC PLASTIC MATERIAL AND METHOD FOR MAKING THE SAME  Inventor: Henry M. Grotta, Delaware, Ohio  Assignee: The United States of America as represented by the Secretary of the Department of Health, Education and Welfare, Washington, DC.
 Filed: June 8, 1970 1'21] Appl. No.: 44,594
 US. Cl 260/9, 117/47 A, 1'l7/62.1, 117/ 138.8 B, 260/17.4 R, 260/17.4 BB, 424/183  Int. Cl. A6lk 17/18, 844d 5/12, C08b 25/00 3,634,123 1/1972 Eriksson et a1. "424/183 3,755,218 8/1973 Yen 117/138.8 E 3,766,104 10/1973 Lyon et a1. 1l7/138.8 E
OTHER PUBLICATIONS Scott, J. E., The Reaction of Long-Chain Quaternary Nl-l4 Salts with Acidic Polysaccharides," Chemistry and Industry No. 7, Feb. 2, 1955, pp. 168-169 [TPl- S63].
Primary Examiner-William H. Short Assistant ExaminerEdward Woodberry 5 7] ABSTRACT Novel water-insoluble, organic solvent-solub1e, long chain alkyl quaternary ammonium salts of heparin, heparinized polymers made therewith, and the method of making the same are disclosed.
15 Claims, N0 Drawings AND METHOD FOR MAKTNTZ TH E SAME This invention relates to nonthrombogenic plastics, and more particularly to plastics made nonthrombogenic by the use of a water-insoluble, organic solventsoluble, long-chain alkyl quaternary ammonium salt of heparin.
It has been known for many years that a basic problem in the development of prostheses for intravascular replacement lies with the complicated processes occurring at the blood-graft interface. The addition of a solid foreign material to the blood stream results in clot formation on that material. This interface activity occurs no matter what the foreign material might be. Porous prosthetics have proven to be useful in the larger vessel, but have failed when adapted to the smaller artery. Certain non-porous materials have been used but also have demonstrated various disadvantages. Solid or imperforate materials are preferred in the field of artificial internal organ development. Pumping chambers, ar-
teries, and materials for encompassing structures having moving parts would demand the property of elasticity as its constituent, prompting an additional requirement of the ideal vascular prosthetic material. It would also be advantageous if that same material could be varied in its elastic properties to the point of rigidity.
Naturally, polymers, both natural and synthetic, and particularly certain synthetic plastics have come to the fore as preferred materials for these prosthetics. Their major drawback, however, is their thrombogenicity. Even though plastics are used in various apparatus such as heart-lung machines, kidney machines, and artificial heart valves and patches, the tendency of these materials to cause coagulation necessitates the use of anticoagulants such as heparin. Even such plastics as Teflon (polytetrafluoraethylene) and the silicone rubbers which are more compatible with blood than most plastics, still show thrombogenic characteristics. The first real advance in the preparation of nonthrombogenic materials was described by Dr. Vincent Gott. The method used by Dr. Gott comprised treating a graphited surface first with Zephiran (benzalkonium chloride) and then with heparin. Materials treated in this way were nonthrombogenic in vivo for long periods of time. The major disadvantage, however, with these materials, was that the method could only be practiced on rigid plastics and a need still exists for a suitable flexible nonthrombogenic plastic, as well as a method of producing the same.
Various methods have been devised for producing such a material, most of which involve chemically bonding a quaternary ammonium salt to the polymer and then heparinizing the same. Usually, this is done by incorporating an amine in the polymer, quaternizing the amine, and then heparinizing the quatemized material. The disadvantages associated with these methods are numerous. The materials prepared by these methods have usually been satisfactory on a small laboratory scale, but could not easily be scaled up to a practical method. Furthermore, these methods were quite satisfactory for preparation and evaluation of individual polymers, the techniques varying from polymer to polymer. A major drawback, based on these differences in techniques, is that heparinization of a composite structure containing more than one type of polymer could not be easily done. Moreover, many of the techniques involve several steps requiring a variety of reagents, solvents,-and reaction conditions. The present invention is designed to eliminate these various problems.
Accordingly, itis a primary object of the present invention to provide a nonthrombogenic plastic material which can be easily and efficiently made.
It is another primary object of the present invention to provide a composition for imparting nonthrombogenic characteristics to polymers.
If is yet another primary object of the present invention to provide a method for the production of nonthrombogenic plastic materials.
It is a further object of the present invention to provide a water-insoluble, organic solvent-soluble, long chain alkyl quaternary ammonium salt of heparin having nonthrombogenia properties.
It is another object of the present invention to provide polymers having a water-insoluble, organic solvent-soluble long chain alkyl quaternary ammonium salt of heparin incorporated therein to thereby provide said polymers with nonthrombogenic properties.
Other objects of the present invention will become apparent as the description thereof proceeds.
Consistent with the foregoing objects, a composition of matter comprising a water-insoluble, organic solvent-soluble, plastic-compatible, long chain alkyl quaternary ammonium salt of heparin is provided. The salt has 2 to 4 long chain alkyl groups attached to the nitrogen atom, the alkyl groups having from about 10 to about 30 carbon atoms. The alkyl groups can be like or unlike. These compounds are generally obtained by heating together a tertiary amine and an alkylating agent to thereby produce the quaternary ammonium salt. To produce the nonthrombogenic plastic, the polymer is exposed to the water-insoluble quaternary ammonium salt in an organic solvent after which it is dried and exposed to a solution of heparin. Such materials have been shown 'to possess in vitro and in vivo nonthrombogenic properties. Suitable polymers, for example, are the following:
Natural rubber Polyvinyl chloride Acrylics.
Polyethylene Polypropylene Ployurethanes Polycarbonates Polystyrenes Polytetrafluoroethylene Silicone rubber Polyesters Nylons EXAMPLE I Tridodecylmethylammonium Chloride Tridodecylmethylammonium chloride (TDMAC) was prepared according to the following scheme:
35 12Hzs)aN CHaCI n zshNCI-I 91 A suitable autoclave was loaded with tridodecylamine and then with at least a molar excess of methyl 3 chloride. The two materials were heated together at 80 C. for approximately 4 hours. Excess methyl chloride was vented and the contents crystallized from petroleum ether. A white waxy solid melting at 60 C. was obtained in better than 90 percent yield.
EXAMPLE II An alternate procedure consisting of heating tridodecylamine with an excess of methyl iodide at reflux temperature and ambient pressure was followed.
EXAMPLE III The procedure of Example 2 was followed in order to make tetradodecyl ammonium chloride. Tridodecylamine and dodecylbromide were heated together at least over night at temperatures of approximately 150 C. A solution of the bromide salt was then passed through an ion exchange column packed with Dowex lX-8. The resulting compound was recrystallized from tetrahydrofuran.
EXAMPLE IV 1,2-Ethylene bis-tridodecylammonium bromide was prepared as follows:
, EXAMPLE V The following scheme as in Example I was used to prepare tridodecyl benzylammonium chloride:
Tridodecyl amine was heated with an excess of benzyl chloride at approximately 150 C. for several hours. The resultant salt was crystallized from tetrahydrofuran.
( nHmOlN EXAMPLE VI The compound 1,5-Pentane bistridodecylammonium chloride was prepared according to the procedure of Example ll:
An excess of tridodecyl amine (Eastman) and 1,5- -diiodopentane (Eastman) were heated together overnight at 150 C. The resulting compound was passed through an ion exchange column (chloride form of Dowex IX-8) using methyl alcohol as the medium andthe compound was crystallized from tetrahydrofuran.
EXAMPLE VII An oil soluble complex of heparin and TDMAC was prepared by vigorously shaking together a toluene or toluene/petroleum ether solution of TDMAC and a water solution of sodium heparinate. Weight ratios of TDMAC/Heparin ranging from 5:1 to 1:1 were used.
EXAMPLE VIII Tridodecylmethyl ammonium iodide was prepared by the following procedure:
Tridodecylamine (13.3 g) and methyl iodide (58.4 g) were mixed and began to reflux exothermically. The mixture was cooled with ice for afew minutes and then allowed to reflux. The exothermic reaction lasted about 5 minutes. Thereafter, the mixture was heated and allowed to reflux for 1% hours. Excess methyl iodide was evaporated on a rotary evaporator, thereby leaving a 1 soft solid which was insoluble in water. The yellow solid was recrystallized from heptane to give a yellow solid which, after drying in a vacuum oven, resulted in 14.8 grams of a brown, waxy material.
EXAMPLE IX Tridodecylmethylammonium nitrate was prepared by the following procedure:
Tridodecylmethylammonium iodide (14.8 g), as prepared by the method of Example VIII, was dissolved in ml of ethanol. Silver nitrate (5.2 g), in excess of that theoretically needed, was dissolved in ml of ethanol on refluxing. The hot silver nitrate solution was poured into the tridodecylmethylammonium iodide solution and, after digesting 4 minutes on a hotplate, the silver iodide precipitate was filtered off to give a clear, colorless solution. The silver iodide precipitate was rinsed twice with ethanol and the washings combined with the previous filtrate.
The solution was evaporated on a rotary evaporator leaving a viscous oil which had small particles of silver iodide suspended in it. The oil was taken into chloroform, filtered, and the filtrate was extracted four times with distilled water, reserving the water phase. The chloroform phase was filtered and then evaporated on a rotary evaporator. Ethanol was added several times to remove water, and finally stripped at 55 C for several hours to give 12.66 g of a white cheesey solid which was then dried in a vacuum oven at 50 C over night.
EXAMPLE x C Tagged TDMAC In order to prepare tagged TDMAC, the following reaction scheme was followed:
Labeled C*I-I I was purchased from Nuclear- Chicago. The iodide was refluxed with tridodecylamine (Eastman) for several hours and the iodide salt exchanged for chloride ion as outlined in the Example 10.
The tagged TDMAC was used in several tests de- CtHKOH L CHBOI H20 wi l scribed more fully hereinbelow.
B EXAMPLE xn [jCy fEQgNQF lPlQ 10 Various polymers-were treated to render them nonthrombogenic. The polymers treated were polyure- Labeled C*I-I OI-I was purchased from Nuclearmane Silicone rubber, yP py i Polyethylene, Chicago. The alcohol was refluxed with concentrated Polycarbonate, Polyvmylehlende, p y y i P acid containing a catalytic concentration of zinc chlotets Such as Mylar, Teflon, y methfimethaerylate ride. Theoff gases were trapped through a caustic andaeopolymet polyealibonate and Silicone rubbertower to an acetone-Dry Ice bath. The synthesized The method used, each Instance, was as fOIIOYVSI C*I-I Cl was then loaded into an autoclave with an ex- The P y was eXROSed to f Percent Solution O cess of tridodecylamine and heated to 80 C for 15 the quaternary amtnenlum Salt elther toluene; P I hours. At the end of this period, the autoclave was leum ether mlxture 0f the two, for apprexlmately opened and recharged with unlabeled CH CI in excess. 4 hours at It shu1d be clearly understood that This was then heated to 80C for an additional 4 hours. any non-Polar e Solvent could be e The P y- The resultant TDMAC was crystallized once from pemer was e f and t Placed a Pe troleum ether and used cent solution of sodium heparmate 11'! a solvent consisting of equal amounts of methanol and water for 4 EXAMPLE XI 25 hours. The treated polymer was then removed, dried, An alternate scheme for preparation of tagged and tested for thrembegemeltY- TDMAC gave better yields: w EXAMPLE XI 8 different polymers were treated with tridodecylme- C'HSI (CHHMN [wnHm 6 a thylammonium chloride and heparin, generally followion exch nge ing the procedure of Example Xll. In order to more easily determine the properties of the treated polymers, 6B 1 9 S-labeled heparin was used. In vitro tests were then N C1 made. The results are shown in Table 1.
TABLE 1 EVALUATION OF PROCEDURES (1) FOR THE HEPARINIZATION OF MATERIALS USING TRIDODECYLMETHYLAMMONIUM CHLORIDE (TDMAC) Materials TDMAC EXPOSURE CONDITIONS Solution Temperature Compatibility Thickness (2) Stability (3) After 3 hr Concentration "C In l/itro, min. of bound percent in Plasma,
heparin remaining percent Initial remaining Silicone Rubber l Ambient No clot 400 67 Silicone Rubber 3 Ambient do. 1,100 9] Silicone Rubber 5 Ambient do. L700 92 Silicone Rubber 7 Ambient do. 2,200 9l Silicone Rubber 1 do. 400 El Silicone Rubber 3 50 do. l,l00 93 Silicone Rubber 5 50 do. L800 95 Silicone Rubber 7 50 do. 2,200 94 Polyurethane 1 Ambient do. 8,300 98 97 Polyurethane 3 Ambient do 15,400 I00 96 Polyurethane 5 Ambient do. 22,600 99 96 Polyurethane 7 Ambient do. 18,600 I00 98 Polypropylene 1 Ambient 18 30 52 82 Polypropylene 3 Ambient 25 85 87 81 Polypropylene 5 Ambient 35 300 33 84 Polypropylene 7 Ambient No clot 820 92 9t Polypropylene l 50 26 I90 91 83 Polypropylene 3 50 26 H0 93 89 Polypropylene 5 50 No clot 830 .90 Polypropylene 7 50 No clot L500 95 99 Polyethylene l Ambient No clot 500 94 94 Polyethylene 3 Ambient No clot L500 I00 95 Polyethylene 5 Ambient No clot L700 I00 95 Polyethylene 7 Ambient No clot 2.500 94 Polyethylene l 50 No clot 300 I00 91 Polyethylene 3 50 No clot 700 98 92 Polyethylene 5 50 No clot v LlOO 96 92 TAB LE 1 Continued Materials TDMAC EXPOSURE ONDITIONS Solution Temperature Compatibility Thickness (2) Stability (3) After 3 hr Concentration C In Vitro, min. of bound percent in Plasma,
heparin remaining percent Initial remaining Polyethylene 7 50 No clot 1,100 100 92 Polyvinyl Chloride 1 Ambient No clot 700 95 I (Rigid) 3 Ambient No clot 1,400 88 94 Polyvinyl Chloride Ambient No clot 2,900 I00 96 Polyvinyl Chloride 7 Ambient No clot 2,500 100 95 Polyvinyl Chloride l 50 No clot 100 I00 63 Polyvinyl Chloride 3 50 No clot 400 100 85 Polyvinyl Chloride 5 50 No clot 1,200 100 88 Polyvinyl Chloride 7 50 No clot 500 95 86 Polycarbonate 1 Ambient No clot 700 I00 86 Polycarbonate 3 Ambient No clot 600 93 88 Polycarbonate 5 Ambient No clot 700 48 89 Polycarbonate 7 Ambient No clot 400 93 90 Polycarbonate I 50 No clot 400 84 88 Polycarbonate 3 50 No clot 500 93 88 Polycarbonate 5 50 No clot 1,100 100 91 Polycarbonate 7 50 No clot 1,800 98 89 Mylar I Ambient 225 91 85 Mylar 3 Ambient No clot 960 92 91 Mylar 5 Ambient No clot 1,030 93 91 Mylar 7 Ambient No clot 1,800 95 90 Mylar 1 50 No clot 500 93 78 Mylar 3 50 No clot 2,200 94 79 Mylar 5 50 No clot 3,900 95 88 Mylar 7 50 No clot 5,250 95 78 Teflon 1 Ambient 20 40 89 78 Teflon 3 Ambient 40 90 93 85 Teflon 5 Ambient 80 89 60 Teflon 7 Ambient I30 89 86 Teflon l I8 30 88 84 Teflon 3 S0 24 50 95 86 Teflon 5 50 26 80 99 79 Teflon 7 50 31 1 I0 99 87 Teflon 3 100 No clot 6,900 96 Teflon 7 100 No clot 9,500 I00 (1) Common procedure in all cases involved a 3-hour exposure to a toluene/petroleum ether solution of TDMAC. Heparinization accomplished at ambient temperature using V4 percent heparin in 50/50 MeOH/H,O.
(2) Measured using S labeled heparin and assuming a density of 1.0 for the heparin coating.
(3) Percent "'S labeled heparin present after exposure to 37 C flowing physiological saline for 100 hours.
It can be seen that in each case, with the exception 5 of polycarbonates, the greater concentration of TDMAC in the organic solvent produced greater heparin layer thickness. In general, temperature increases also produced substantial increases in amounts of f1- nally bonded heparin. A 50/50 mixture of toluene/petroleum ether proved to be a preferred solvent system because of the ease with which it could be subsequently eliminated from treated objects. Other organic solvents could, of course, be used.
It can also be seen that large quantities of heparin can be bound at the surface of a large variety of materials. This great amount of heparin appears to be quite strongly bonded as evidenced by the exceptionally good stability to normal saline (100 hours) and plasma (3 hours). Retention of greater than 90 percent of the originally bonded heparin can be attained with all of the materials evaluated. V
EXAMPLE XIV Microscopic examination of TDMAC-heparin treated silicone rubber surfaces revealed that gross quantities of the TDMAC were deposited thereby causing surface roughness. Removal of this gross deposit was attempted by selective solvent extraction before heparinization. Solvent systems investigated included: methanol, ethanol, acetone, formamide and petroleum ether. The treatment consisted in steeping silicone rubber materials in a 7 percent TDMAC solution. The samples were dried, exposed to the various solvents for one-half hour, and then heparinized in a /25 methyl alcohol/heparin solution (0.25 percent heparin). Table 2 shows how much heparin was adsorbed by TDMAC surfaces so treated and the stability of said surfaces to saline and plasma.
TABLE 2 SELECTED SOLVENT TREATMENT OF TDMAC SURFACES He arin Thickness TABLE, 2 Continued SELECTED SOLVENT TREATMENT OF TDMAC SURFACES He arin Thickness Compatibility,
It is evident from this Table that this technique deleteriously affects not only the compatibility of the treated surface (with the exception of the formamide rinse), but also the environmental stability of the surface. These failures are possibly attributable to certain physical properties of TDMAC, particularly its soft, wasy nature. Presumably, the material is eroded mechanically under body conditions, 37 C, and in environment of highturbulence within the vascular system.
EXAMPLE XV To confirm the hypothesis that the material is eroded mechanically, treated plastic flags were subjected to an environment of flowing saline solution at 37 C. For these experiments, flags approximately 16 X 20 mm were prepared and then treated with S or H radiolabeled heparin, or *C labeled TDMAC as prepared in Examples X or XI. The data obtained with the S- labeled heparin patches is set forth in Table 3.
TABLE 3 IN VITRO STABlLlTY OF TDMAC TREATED SURFACES TO FLOWING SALlNE AT 37 C Heparin Thickness It is clear from these data that greater quantities of heparin are lost from exposure to turbulent flow of saline than that from static in vitro exposure normally employed.
EXAMPLE XVI Solution applied coatings which can be later heparinized were easily prepared from TDMAC and polyurethane. The solutions consisted of approximately 90 percent polyurethane (coating grade) and percent TDMAC dissolved in a mutual solvent, such as tetrahydrofuran. Solids content of the coating solution was kept at approximately 10 percent. Aluminum disks were coated with the above material, dried, then exposed to 0.25 percent heparin solutions in 50/50 methyl alcohol/water. Materials heparinized this way did not produce clots during 60 minutes in our modifled Lee-White clotting test. The addition of thromboplastin at the end of this period produced clots within 60 seconds, thereby indicating that no appreciable quantities of heparin were extracted by the blood during the test period. Parallel experiments with S- labeled heparin indicated that a layer of heparin approximately 5,400 A was present at the surface. Stability tests indicated that 98 percent of the heparin remained after exposure of the surfaces to isotonic saline for 100 hrs. and 82 percent after exposure to blood plasma for 4 hrs. Nevertheless, heparin coatings 4,400 A thick are still adequate for nonthrombogenic effects.
EXAMPLE XVII In an effort to determine the chemical nature of the TDMAC/heparin surface, an investigation was undertaken to determine amounts of each substance (TDMAC and heparin) present at the surface of a material such as silicone rubber when treated via the pro- I cess of this invention. To accomplish this, C labeled TDMAC and S labeled heparin were used. It was deterrnined that approximately 30 moles of TDMAC per tetrasaccharide unit of heparin is present at the surface.
EXAMPLE XVIII Plasma was passed over a radiolabeled heparinized surface TDMAC surface and the eluate analyzed. Small quantities of heparin were removed (2-4 mg./ml.). However, the amounts were insufficient to constitute an anticoagulant level of heparin in the blood 25 ug./ml.). There also was an increase in eluted heparin when saline followed the plasma flows. This has been a consistent observation using this technique.
To further investigate the cause of the eluted heparin in the saline fractions, the experiment was repeated with C labeled TDMAC. The TDMAC-heparin complex was removed in small quantities (20-40 ug./ml.) by the plasma. Removal essentially stopped when saline followed the plasma flows. However, 4 N sodium chlo ride solution caused elution of substantial quantities of C labeled material.
The ratio of heparin tetrasaccharide units to TDMAC and S labeled heparin was 1:21. These. results are in line with previous work using other quaternary ammonium binding salts and suggests that steric factors may limit the amount of heparin which is bound at the surface of materials.
Very dramatic effects of TDMAC surfaces on lipids and lipoproteins were detected in initial plasma fractions which contacted these surfaces. These effects are illustrative of the general trend for individual components such as cholesterol, fatty acids, phospholipids, triglycerides, and a and B lipoproteins. These data strongly suggest that the greatest interactions occur with surfaces containing high concentrations of pure TDMAC. The heparinization of these surfaces lowered the adverse effects substantially. Washing the heparinized surface with a solvent for TDMAC such as formamide or alcohol reduced these interactions even further.
EXAMPLE XIX The effect of TDMAC surfaces on platelet adsorption, aggregation, and disruption was also studied. Table 4 contains the data on platelet aggregation."
As shown in Table 4, aggregation is most severe when platelets were exposed to surfaces containing excesses of the TDMAC. These data are in line with what was expected. The greater the quantities of free quaternary ammonium salts (positive surfaces) used, the greater the aggregation produced. However, these results do not present the whole picture, since they do not indicate the quantities of adsorbed platelets. Platelets were adsorbed in all cases and this is shown in Table 5. Tables 6 and 7 indicate levels of acid phosphatases and platelet factor 111 which were released into the plasma by ruptured platelets. As indicated from these Tables,
platelet rupture was minimal where precautions were' taken qzsms 23295 quan ies o TDMA TABLE 4 UIABLEV Fraction No.
' Done by Bochringer-Mannheim Reagents mU Amount of enzyme required to convert 1 1:. mole of substrate/min at 30 C.
AGGREGATION OF PLATELETS EXPOSED TO TDMAC SURFACES Percent Particles in Individual Platelet and Aggregated Platelet Size Ranges Heparinized Fraction TDMAC Hep. TDMAC TDMAC Washed Numbers 1nd. Agg. Incl. Agg. 1nd. Agg.
Standard Platelet rich plasma 98.8 1.3 99.0 0.8 99.2 0.8
TABLE 5 TABLE 7 PLATELET ADSORPTION' OF SELECTED PLATELET-RICH PLASMA FRACTIONS SUBSEQUENT TO EXPOSURE V STYPVEN CLOTTING TIMES (PF 111) OF PLATELET-POOR u 0W1 i 0 TR ATED lLlCNE Clotting Time iseconds) of 1:10 Dilution H t let m 3 Fraction No. 13 No. 35 No. 16 e S m N0. Pure TDMAC Hep. TDAB Hep. TDMAC Fraction Column 13 Column 8 Column 16 Form Rinse Numbers Pure TDMAC Hep. TDMAC Hep. TDMAC 55 Standard 95 100 90 Standard 403,000 543,000 638,000 5 105 100 5 19,000 97,000 51 1,000 10 60 90 10 15,000 298,000 594,000 15 1 15 85 15 8,000 470,000 622,000 g? 11 g2 g2 20 8,000 486,000 561,000 25 66,000 540,000 60 30 v 90 30 360,000 494,000 576,000 35 369,000 585,000 23 ,3; $3 40 69,000 514,000 540,000 45 85 85 45 0 85 50 540,000 Lysed prep 55 65 control 30 30 25 Detected by Coulter Counter. TDMAC silicone rubber with formamide rinse.
v Some dilution from the initial saline flows was obvious in this fraction Platelet-poor plasma spun after exposure prior to assays. TDAB is tetradodecylammonium bromide.
EXAMPLE XX In addition to studies on the effect of TDMAC surfaces on platelets, levels of selected clotting factors were determined. A summary of the prothrombin and TABLE 9 RESULTS OF THROMBUS FORMATION ON VENA CAVAL IMPLANT RINGS COATED WITH TDMAC-HEPARIN Amount of Date of Thrombus Material Implant Sterilization in Lumen Comments TDMAC Heparin 11-2-67 TDMAC CLEAR do. do. do. 0 CLEAR do. 1 1-6-67 do. 0 CLEAR do. 1 1-10-67 do. 0 sacrificed after 2 weeks clear do. 1 l-28-67 do. 0 do. do. do. do. 0 do. do. 1 l-30-67 do. 0 do. do. l-19-68 do. O do.
partial thromboplastm times are included in Table 8. EXAMPLE XXII As shown in this Table, extrinsic factors were affected in initial fractions of plasma contacting TDMAC sur- 25 faces. However, the levels soon returned to normal. The intrinsic system was affected when plasma contacted other surfaces such as glass or heparinized sili- 00116 rubber anotherroute.
The work on the use of water insoluble quaternary ammonium salts with heparin was extended from TDMAC to other structurally similar compounds. Included in this examination were tetradodecylammonium chloride and bromide, tridodecylbenzylam- TABLE 8 PLASMA CLOTTING FACTOR MEASUREMENT SUBSEQUENT TO EXPOSURE OF PLASMA TO VARIOUS SURFACES Clotting Tests Clotting Times", Seconds Prothrombin Time Partial Thromboplastin Column Fraction No. (PT) Time (PTT) 35 Std 14.0 67.0 Glass Beads 11.0 No clot 12.0 No clot 12.0 No clot '20 l 1.5 No clot 25 12.0 No clot 30 13.0 No clot 34 20.0 No clot 38 Std 1 1.0 73.5 Silicone 3 No clot No clot Rubber 5 No clot No clot Heparinized 10 42.0 No clot TDMAC 15 24.0 No clot 39 Std 14.0 68.0 Silicone rubber 5 14.0 No clot polystyrene 10 l 1.0 No clot graft, chloro- 15 13.0 82.0 methylated 20 12.0 109.0 aminated 25 12.0 No clot heparinized 30 12.0 No clot 35 12.0 No clot 37 12.0 No clot Platelet-free plasma prepared from ACD whole blood. Average of 24 tests/sample. v V I.
EXAMPLE XXI momum chloride, 1,2-ethylene b18- Acute and chronic tests of the in vivo performance tridodecylammonium bromide, and 1,5-pentane bisof TDMAC heparinized surfaces indicate the method to be very promising. Table 9 shows the results of the. vena caval ring implant tests.
tridodecylammonium chloride. Table 10 indicates some preliminary data which was obtained on these salts.
TABLE 10 CHARACTERISTICS OF SILICONE RUBBER SURFACES IMPREGNATED WITH VARIgXETQSUATERNARY AMMONIUM Salt Thickness Stability Clotting of Bound remaining) Time Heparin.
Tetradodecylammonium Silicone rubber impregnated with a solution of the salt (I()%) in tetrahydrofuran or 50/50 toluene/methyl alcohol.
Measured using S labeled heparin and assuming a density of L for the heparin coating.
Percent S labeled heparin present after exposure to 37 C flowing physiological saline for 100 hours.
Measured using modified Lee-White coagulation tests. NC no clot after 60 min. of testing.
Second NC indicates no clot after addition of thromboplastin; 60 indicates a clot formed within 60 seconds after addition. V a V These materials were tested in vitro with flowing plasma as well as saline. The elution of bound heparin by plasma is somewhat higher (6-20 ,ug/cc) than the TDMAC surfaces described earlier, and is sufficient to anticoagulate the blood. This conclusion is supported TDMAC-heparin complexes as prepared by the by our in vitro coagulation test. Whole blood contacted method of Example VII were used to plasticize silicone for one hour with these surfaces does not produce a u C pl ta g ryi g ra s f clot upon the addition of two drops of thromboplastin. TDMAC heparin were used- The results of in vitro Blood contacting a surface heparinized by means of the 30 tti gt tg Sh in Table TABLE 12 OLEOPHILIC I-IERRIN/TDMAC COMPLEX FORMATION TDMAC/Heparin Agitation Time" Complex Heparin Clotting Time Ratio EXAMPLE XXIV min. Yield, Content min/sec.
/ l l 94 I7 16/- 5/l I0 95 l7 l6/ 3.6/1 1 70 NC/NC 2.5/1 1 86 31 NC/NC l .7/l l 76 39 NC/NC 1.7/1 30 76 48 NC/NC l/l l 62 NC/NC TDMAC dissolved in a 50/50 mixture of toluene/petroleum ether was shaken with a water solution of heparin in a separatory funnel.
2 Silicone rubber impregnated with a 7% solution of the complex then dried. Recalcified whole human blood was then contacted for 1 hr. after which thromboplastin was added.
NC=noclot. V M t. .4. um. been... 1,5 difunctional salt does cloton the addition of throm- From this Table it can be seen that a silicone rubber boplastm, indicating no significant elution of heparin impregnated with a complex having a heparin content by the blood. of about 30 percent would perform as a nonthrombo- EXAMPLE XXIII genic surface. The failure of contacted blood to clot variousspolymers were treated with tridocecylme 50 after the thromboplastin is added indicates that some heparin is being leached from the surface of the matethylammomum nitrate (TDMAN) m the Same manner rial. In order to determine the extent of heparin elution,
as previously treated with TDMAC. The results are an 35S tagged heparin complex was p p and wn T l Sho m ab 6 l 1 TABLE 1 l posed to water and to blood plasma in our standard elution test. After a 100-hour ex osure to water, 96 cr- 5 5 v P P NONTHROMBOGENlC PROPERTlES OF MATERIALS cent of the he arm remained, and after a 3-hour ex 0- HEPARlNlZED p p 7 WITH TDMANm sure to blood plasma, 90 percent was retained. When moodrcomgmibimv m the coagulation test was re-run, using platelet rich figg s g ssg plasma in place of whole blood, a control silicone rub- Mmerial minute's seconds ber surface caused the plasma to clotafter 20 minutes I of exposure. The complex treated disks did not clot gg g g gg figgg 3 after 1 hour of exposure, but did clot within 60 seconds Polypropylene NC 40 after the addition of thromboplastin. This suggests that 38 a component of whole blood not present in platelet rich Polyvinyl chloride NC 30 plasma IS the elutmg agent. Aluminum C 35 It will now be apparent from the foregoing detailed All materials were soaked in a l0% toluene solution of TDMAN, dried. then description that the objects set forth at the outset of heparinized using 0.25% heparin in lzl methyl alcohokwater. thi ifi ti h b f ll hi d ""Tridodecylammnnium nitrate. Per modified Lee-White coagulation test; NC no clot in 60 minutes. through unhzatlon of the present lnventlon whlle there is shown and described a present preferred embodiment of the invention, it is to be distinctly understood that the invention is not limited thereto, but may be otherwise variously embodied and practiced within the scope of the following claims.
What is claimed is:
1. A method of making a nonthrombogenic plastic material comprising the steps of exposing a polymeric plastic to an organic solvent solution of waterinsoluble, organic solvent-soluble, plastic-compatible long chain alkyl quaternary ammonium salt at ambient temperature, said long-chain alkyl quaternary ammonium salt having from 2 to 4 alkyl groups each having from about to about 30 carbon atoms, and thereafter exposing said polymer to a solution of heparin at ambient temperature.
2. The method of claim 1, wherein said 2 to 4 alkyl groups have 12 carbon atoms.
3. The method of claim 2, wherein said quaternary ammonium salt is selected from the group consisting of tridodecylmethyl ammonium salts, tetradodecyl ammonium salts, 1,2-ethylene-bis-tridodecyl ammonium salts, tridodecylbenzyl ammonium salts, and l,5-pentane-bis-tridodecyl ammonium salts.
4. The method of claim 1, wherein said plastic is a member of the group consisting of polyethylene, polypropylene, polyurethanes, polycarbonates, polytetrafluoroethylene, silicone rubber, polyesters, nylons, natural rubber, polyvinyl chloride, acrylics, polystyrene, and a copolymer of polycarbonate and silicone rubber.
5. The method of claim 1, wherein said organic solvent solution of said quaternary ammonium salt is a 10 percent solution.
6. The method of claim 5, wherein said organic solvent is selected from the group consisting of toluene,
petroleum ether, and mixtures thereof.
7. The method of claim 1, wherein said plastic is exposed to said organic solvent solution for from about 3 to about 4 hours. 8. The method of claim l, wherein said solution of heparin is a 0.25 percent solution of sodium heparinate.
9. The method of claim 8, wherein said sodium heparinate is dissolved in a mixture of methanol and water.
10. The method of claim 1 wherein said plastic is exposed to said solution of heparin for about 4 hours.
11. The method of claim 1, wherein said plastic is dried subsequent to being exposed to said solution of quaternary ammonium salt and prior to being exposed to said solution of heparin.
12. A nonthrombogenic plastic material having incorporated therein a complex of heparin and a watersolvent-soluble, plastic-compatible long chain alkyl quaternary ammonium salt applied by the method of claim 1.
13. A plastic material according to claim 12, wherein said 2 to 4 alkyl groups have 12 carbon atoms.
14. A plastic material according to claim 13, wherein said quaternary ammonium salt is selected from the group consisting of tridodecylmethyl ammonium salts, tetradodecyl ammonium salts, 1,2-ethylene-bistridodecyl ammonium salts, tridodecylbenzyl ammonium salts, and l,5-pentane-bis-tridodecyl ammonium salts.
15. A plastic material according to claim 12, wherein said plastic is a member of the group consisting of polyethylene, polypropylene, polyurethanes, polycarbonates, polytetrafluoroethylene, silicone rubber, polyesters, nylons, natural rubber, polyvinyl chloride, acrylics, polystyrene, and a copolymer of polycarbonate and silicone rubber.
|Cited Patent||Filing date||Publication date||Applicant||Title|
|US3617344 *||5 Aug 1966||2 Nov 1971||Us Health Education & Welfare||Nonthrombogenic plastic surfaces and preparation thereof|
|US3634123 *||21 Jun 1968||11 Jan 1972||Jan Christer Eriksson||Method for making nonthrombogenic surfaces|
|US3755218 *||14 Aug 1970||28 Aug 1973||California Inst Of Techn||Ionically bonded block elastomeric copolymers of a polyquaternary polyurethane and heparin|
|US3766104 *||19 May 1971||16 Oct 1973||Rhone Poulenc Sa||Non thrombogenic polymers containing quaternary ammonium groups to which molecules of heparin are bonded|
|1||*||Scott, J. E., The Reaction of Long Chain Quaternary NH 4 Salts with Acidic Polysaccharides, Chemistry and Industry No. 7, Feb. 2, 1955, pp. 168 169 TPI S63 .|
|Citing Patent||Filing date||Publication date||Applicant||Title|
|US3987797 *||11 Dec 1974||26 Oct 1976||Ethicon, Inc.||Antimicrobial sutures|
|US4046725 *||16 Sep 1976||6 Sep 1977||Rhone-Poulenc Industries||Polyurethanes for articles for medical usage|
|US4116898 *||31 Jan 1977||26 Sep 1978||Becton, Dickinson And Company||Non-thrombogenic articles|
|US4239664 *||31 Oct 1978||16 Dec 1980||Research Corporation||Anti-thrombogenic PVP-heparin polymer|
|US4265927 *||10 Jul 1978||5 May 1981||Aminkemi Ab||Method of heparinizing a charged surface of a medical article intended for blood contact|
|US4291133 *||5 Apr 1979||22 Sep 1981||Vaclav Horak||Nonthrombogenic polymer surface|
|US4302368 *||17 Sep 1979||24 Nov 1981||Becton, Dickinson And Company||Nonthrombogenic articles and method of preparation|
|US4349467 *||17 Sep 1979||14 Sep 1982||Williams Joel L||Nonthrombogenic articles and method of preparation|
|US4353996 *||23 Sep 1980||12 Oct 1982||Snamprogetti, S.P.A.||Bio-compatible porous fibres and materials for occluding biologically interesting substances, and method for their manufacture|
|US4521564 *||10 Feb 1984||4 Jun 1985||Warner-Lambert Company||Covalent bonded antithrombogenic polyurethane material|
|US4530974 *||13 Jul 1982||23 Jul 1985||Board Of Regents, The University Of Texas System||Nonthrombogenic articles having enhanced albumin affinity|
|US4588624 *||13 May 1983||13 May 1986||Astra Meditec Ab||Articles exhibiting a biocompatible surface layer|
|US4600652 *||1 Apr 1985||15 Jul 1986||Warner-Lambert Company||Permanently bonded antithrombogenic polyurethane surface|
|US4613517 *||12 Aug 1985||23 Sep 1986||Becton, Dickinson And Company||Heparinization of plasma treated surfaces|
|US4673584 *||5 Mar 1986||16 Jun 1987||Astra Meditec Ab||Process for providing articles with a biocompatible surface layer|
|US4676975 *||7 Dec 1984||30 Jun 1987||Becton, Dickinson And Company||Thermoplastic polyurethane anticoagulant alloy coating|
|US4678660 *||14 Aug 1985||7 Jul 1987||Deseret Medical, Inc.||Thermoplastic polyurethane anticoagulant alloy coating|
|US4713402 *||30 Aug 1985||15 Dec 1987||Becton, Dickinson And Company||Process for preparing antithrombogenic/antibiotic polymeric plastic materials|
|US4725279 *||28 May 1985||16 Feb 1988||Sterling Drug Inc.||Bio compatible and blood compatible materials and methods|
|US4786556 *||24 Jul 1987||22 Nov 1988||Becton, Dickinson And Company||Polymeric articles having enhanced antithrombogenic activity|
|US4820302 *||25 Jun 1982||11 Apr 1989||Sterling Drug Inc.||Bio compatible and blood compatible materials and methods|
|US4820811 *||4 Dec 1986||11 Apr 1989||Research Corporation||Amine reacted therapeutic agents|
|US4828561 *||22 Apr 1982||9 May 1989||Sterling Drug Inc.||Bio compatible and blood compatible materials and methods|
|US5053048 *||8 Nov 1990||1 Oct 1991||Cordis Corporation||Thromboresistant coating|
|US5073171 *||12 Jan 1989||17 Dec 1991||Eaton John W||Biocompatible materials comprising albumin-binding dyes|
|US5135516 *||15 Dec 1989||4 Aug 1992||Boston Scientific Corporation||Lubricious antithrombogenic catheters, guidewires and coatings|
|US5182317 *||17 Jun 1991||26 Jan 1993||Cardiopulmonics, Inc.||Multifunctional thrombo-resistant coatings and methods of manufacture|
|US5262451 *||5 Jul 1988||16 Nov 1993||Cardiopulmonics, Inc.||Multifunctional thrombo-resistant coatings and methods of manufacture|
|US5270046 *||6 Nov 1991||14 Dec 1993||Ube Industries, Ltd.||Heparin bound anti-thrombotic material|
|US5338770 *||12 Apr 1990||16 Aug 1994||Cardiopulmonics, Inc.||Gas permeable thrombo-resistant coatings and methods of manufacture|
|US5342693 *||22 Mar 1993||30 Aug 1994||Cardiopulmonics, Inc.||Multifunctional thrombo-resistant coating and methods of manufacture|
|US5451424 *||24 Nov 1992||19 Sep 1995||Becton Dickinson And Company||Anti-infective and antithrombogenic medical articles and method for their preparation|
|US5490839 *||22 May 1995||13 Feb 1996||Scimed Life Systems, Inc.||Catheter balloon with retraction coating|
|US5496276 *||22 May 1995||5 Mar 1996||Scimed Life Systems, Inc.||Catheter balloon with retraction coating|
|US5532311 *||1 Feb 1995||2 Jul 1996||Minnesota Mining And Manufacturing Company||Process for modifying surfaces|
|US5541167 *||28 Oct 1994||30 Jul 1996||Baxter International Inc.||Thromboresistant coating for defoaming applications|
|US5583213 *||12 May 1995||10 Dec 1996||Minnesota Mining And Manufacturing Company||Process to activate sulfated polysaccharides|
|US5707366 *||7 Jun 1995||13 Jan 1998||Becton Dickinson And Company||Anti-infective and antithrombogenic medical articles and method for their preparation|
|US5736251 *||20 Dec 1996||7 Apr 1998||Corvita Corporation||Lubricious silicone surface modification|
|US5738901 *||1 Nov 1995||14 Apr 1998||Scimed Life Systems, Inc.||Catheter balloon with retraction coating|
|US5804318 *||26 Oct 1995||8 Sep 1998||Corvita Corporation||Lubricious hydrogel surface modification|
|US5955016 *||6 Jun 1995||21 Sep 1999||Goldfarb; David||Method of forming a vascular prosthetic structure including expanded PTFE and graphite|
|US6120532 *||24 Jul 1992||19 Sep 2000||Goldfarb; David||Graphite impregnated prosthetic vascular graft materials|
|US6146771 *||1 Jul 1997||14 Nov 2000||Terumo Cardiovascular Systems Corporation||Process for modifying surfaces using the reaction product of a water-insoluble polymer and a polyalkylene imine|
|US6197289||1 Jul 1997||6 Mar 2001||Terumo Cardiovascular Systems Corporation||Removal of biologically active agents|
|US6261271||13 Jan 1998||17 Jul 2001||Becton Dickinson And Company||Anti-infective and antithrombogenic medical articles and method for their preparation|
|US6328710||22 Oct 1997||11 Dec 2001||Scimed Life Systems, Inc.||Process improvements for preparing catheter balloons|
|US6436135||24 Oct 1974||20 Aug 2002||David Goldfarb||Prosthetic vascular graft|
|US6630460||9 Feb 2001||7 Oct 2003||Medtronic, Inc.||Heparin compositions and methods of making and using the same|
|US6710147||10 Jun 2003||23 Mar 2004||The Goodyear Tire & Rubber Company||Process for synthesizing tackifier resin|
|US6953625||26 Jun 2003||11 Oct 2005||Medtronic, Inc.||Heparin compositions and methods of making and using the same|
|US7371257||23 Nov 2004||13 May 2008||Boston Scientific Scimed, Inc.||Stent lining|
|US8498682||2 Jul 2010||30 Jul 2013||Glumetrics, Inc.||Optical determination of pH and glucose|
|US8535262||9 Dec 2011||17 Sep 2013||Glumetrics, Inc.||Use of an equilibrium intravascular sensor to achieve tight glycemic control|
|US8700115||15 May 2013||15 Apr 2014||Glumetrics, Inc.||Optical sensor configuration for ratiometric correction of glucose measurement|
|US8715589||14 May 2013||6 May 2014||Medtronic Minimed, Inc.||Sensors with thromboresistant coating|
|US8738107||9 May 2008||27 May 2014||Medtronic Minimed, Inc.||Equilibrium non-consuming fluorescence sensor for real time intravascular glucose measurement|
|US8979790||11 Sep 2013||17 Mar 2015||Medtronic Minimed, Inc.||Use of an equilibrium sensor to monitor glucose concentration|
|US8983565||25 Jul 2013||17 Mar 2015||Medtronic Minimed, Inc.||Optical determination of pH and glucose|
|US20040005470 *||26 Jun 2003||8 Jan 2004||Edouard Koulik||Heparin compositions and methods of making and using the same|
|US20050037132 *||24 Apr 2003||17 Feb 2005||Roland Horres||Anti-thrombogenic surfaces and process for their production|
|US20120053427 *||30 Aug 2011||1 Mar 2012||Glumetrics, Inc.||Optical sensor configuration and methods for monitoring glucose activity in interstitial fluid|
|DE2748858A1 *||31 Oct 1977||3 May 1979||Unitika Ltd||Polymer articles prodn. with reduced thrombogenic tendency - by treating with soln. of synthetic fibrinolytic cpd.|
|EP0769503A2 *||16 Oct 1996||23 Apr 1997||Terumo Kabushiki Kaisha||A heparin complex and medical device having such substance|
|WO1983003977A1 *||13 May 1983||24 Nov 1983||Astra Meditec Ab||Articles exhibiting a biocompatible surface layer and process for providing articles with such a surface layer|
|U.S. Classification||523/112, 525/54.2|
|International Classification||A61L33/00, C08B37/10|
|Cooperative Classification||A61L33/0017, C08B37/0075, A61K31/715|
|European Classification||C08B37/00P2G, A61L33/00H2A, A61K31/715|